Effect of cryomilling time on microstructure evolution and hardness of cryomilled AZ31 powders

被引:13
作者
Guan, Dikai [1 ]
Gao, Junheng [1 ,2 ]
Rainforth, W. Mark [1 ]
机构
[1] Univ Sheffield, Dept Mat Sci & Engn, Sheffield S1 3JD, S Yorkshire, England
[2] Univ Sci & Technol Beijing, Beijing Adv Innovat Ctr Mat Genome Engn, Beijing 100083, Peoples R China
基金
英国工程与自然科学研究理事会;
关键词
Cryomilling; AZ31; TEM; XRD; Hardness; Grain refinement; MG ALLOY; NANOSTRUCTURED MATERIALS; THERMAL-STABILITY; HIGH-STRENGTH; NANOCRYSTALLINE; MAGNESIUM; BEHAVIOR;
D O I
10.1016/j.matchar.2021.111311
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The synthesis of nanostructured AZ31 powder by cryomilling was studied in this paper. The microstructural evolution during cryomilling, including the changes of particle morphology and internal grain size, was characterized via optical microscopy, SEM, TEM and XRD. Observations during the cryomilling produced four main findings. Firstly, cryomilling can refine the grains of AZ31 particles down to 100 nm after around 1 h milling and the minimum average grain size of about 30 nm was reached when the cryomilling time was extended to 6 h or longer. Secondly, cold welding played a dominant role in the early stage of cryomilling, while fracture took place in the late stage and surpassed cold welding. The former led to a particle size increase while the latter decreased the particle size. The minimum average particle size after 6 h cryomilling was approximately 26 mu m. Thirdly, a few particles were agglomerated with other particles and could not be processed by cryomilling due to cold welding. Finally, after cryomilling 6 h and longer times, the hardness reached 162 HV which was much higher than other values reported in AZ31 alloy studies.
引用
收藏
页数:9
相关论文
共 41 条
[1]   X-ray peak broadening on microstructure, and structural properties of titanium and Ti-6Al-4V alloys [J].
Ali, Showkat ;
Karunanithi, R. ;
Prashanth, M. ;
Rahman, M. Abdur .
MATERIALS TODAY-PROCEEDINGS, 2020, 27 :2390-2393
[2]   H-sorption behaviour of mechanically activated Mg-Zn powders [J].
Deledda, Stefano ;
Hauback, Bjorn C. ;
Fjellvag, Helmer .
JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 446 (173-177) :173-177
[3]   Mechanical Behavior of Cryomilled CP-Ti Consolidated via Quasi-Isostatic Forging [J].
Ertorer, Osman ;
Zuniga, Alejandro ;
Topping, Troy ;
Moss, Wes ;
Lavernia, Enrique J. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (01) :91-103
[4]   Nanostructure formation by mechanical attrition [J].
Fecht, HJ .
NANOSTRUCTURED MATERIALS, 1995, 6 (1-4) :33-42
[5]   Enhancing ductility and strength of nanostructured Mg alloy by in-situ powder casting during spark plasma sintering [J].
Guan, Dikai ;
Gao, Junheng ;
Sharp, Joanne ;
Rainforth, W. Mark .
JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 769 :71-77
[6]   Thermal Stability of Cryomilled Mg Alloy Powder [J].
Guan, Dikai ;
Rainforth, W. Mark ;
Sharp, Joanne ;
Gao, Junheng .
MAGNESIUM TECHNOLOGY 2017, 2017, :225-233
[7]   On the use of cryomilling and spark plasma sintering to achieve high strength in a magnesium alloy [J].
Guan, Dikai ;
Rainforth, W. Mark ;
Sharp, Joanne ;
Gao, Junheng ;
Todd, Iain .
JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 688 :1141-1150
[8]   Hall-Petch relation and boundary strengthening [J].
Hansen, N .
SCRIPTA MATERIALIA, 2004, 51 (08) :801-806
[9]   Development of nanocrystalline structure during cryomilling of Inconel 625 [J].
He, JH ;
Lavernia, EJ .
JOURNAL OF MATERIALS RESEARCH, 2001, 16 (09) :2724-2732
[10]   DISLOCATION PARTICLE INTERACTIONS IN AN OXIDE DISPERSION STRENGTHENED ALLOY [J].
HERRICK, RS ;
WEERTMAN, JR ;
PETKOVICLUTON, R ;
LUTON, MJ .
SCRIPTA METALLURGICA, 1988, 22 (12) :1879-1884