Effect of pre-oxidation on hot corrosion resistance of HR3C stainless steel in sulfate salt with or without Fe2O3

被引：16
|
作者：
Yu, Zheng [1 ]
Lu, Jintao [2 ]
Chen, Minghui [1 ]
Wang, Jinlong [1 ]
Wang, Fuhui [1 ]
机构：
[1] Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China
[2] Xian Thermal Power Res Inst Co Ltd, Xian 710032, Peoples R China
来源：
CORROSION SCIENCE | 2021年 / 192卷
关键词：
Stainless steel; STEM; Hot corrosion; Sulfidation; BEHAVIOR; TECHNOLOGY; PLATELETS; OXYGEN; NI;
D O I：
10.1016/j.corsci.2021.109789
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
HR3C steel exhibits high oxidation resistance in air at 700 degrees C owing to the formation of a dense chmmia scale. In the presence of sulfate salt deposition (Na2SO4:K2SO4 = 1:1), hot corrosion occurs. It leads to the dissolution and re-precipitation of Cr2O3 platelets and severe internal corrosion. Pre-oxidation can notably enhance corrosion resistance with almost no internal corrosion zone. When the deposited sulfate salt contains Fe2O3 (Na2SO4 : K2SO4:Fe2O3 = 1:1:1), HR3C steel suffers even severer hot corrosion. Its scale spalls off easily and internal corrosion develops deep into the steel. Meanwhile, pre-oxidation played almost no positive effect on corrosion in sulfate salt containing Fe2O3.
引用
收藏
页数：9
相关论文
共 50 条
  • [31] Effect of Al2O3 and enamel coatings on 900°C oxidation and hot corrosion behaviors of gamma-TiAl
    Tang, ZL
    Wang, FH
    Wu, WT
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 276 (1-2): : 70 - 75
  • [32] Effect of the calcination temperature on the properties of Fe2O3/SiO2 catalysts for oxidation of hydrogen sulfide
    Bukhtiyarova, Galina A.
    Delii, Irina V.
    Sakaeva, Nailya S.
    Kaichev, Vasiliy V.
    Plyasova, Ludmila M.
    Bukhtiyarov, Valerii I.
    REACTION KINETICS AND CATALYSIS LETTERS, 2007, 92 (01): : 89 - 97
  • [33] Effect of the calcination temperature on the properties of Fe2O3/SiO2 catalysts for oxidation of hydrogen sulfide
    Galina A. Bukhtiyarova
    Irina V. Delii
    Nailya S. Sakaeva
    Vasiliy V. Kaichev
    Ludmila M. Plyasova
    Valerii I. Bukhtiyarov
    Reaction Kinetics and Catalysis Letters, 2007, 92 : 89 - 97
  • [34] Improvement of Oxidation Resistance of Remelted Zone in an Al2O3-Forming Austenitic Stainless Steel by Annealing
    Zhao, Kai
    Peng, Huabei
    Yang, Xiao
    Wang, Gaixia
    Wen, Yuhua
    OXIDATION OF METALS, 2015, 83 (3-4): : 273 - 290
  • [35] Hot corrosion of the ceramic composite coating Ni3Al-Al2O3-Al2O3/MgO plasma sprayed on 316L stainless steel
    Shirazi, Amir Khodaparast
    Kiahosseini, Seyed Rahim
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2017, 108 (08) : 675 - 680
  • [36] Improving the oxidation resistance by forming continuous Al2O3 protective layer in alumina-forming austenitic stainless steel
    Shi, Jiajian
    Meng, Fanqiang
    Huang, Guoqiang
    Liu, Fangchen
    Zhai, Lihong
    Chen, Yingxue
    Zhang, Feifei
    Lin, Jiming
    Wang, Lei
    SURFACE & COATINGS TECHNOLOGY, 2024, 493
  • [37] Effect of FeCl3 in NaCl-MgCl2 molten salts on the corrosion behavior of 316 stainless steel at 600?C
    Lu, Pengfei
    Liu, Qi
    Bao, Hongliang
    Pan, T. J.
    Tang, Zhongfeng
    CORROSION SCIENCE, 2023, 212
  • [38] Preparation and Corrosion Resistance of an Al2O3/Ni Coating on 316 Stainless Steel in Molten 52MgCl2-48NaCl Chloride Salt
    Wang, Changxuan
    Zhang, Wenjiao
    Wang, Yanli
    CORROSION, 2022, 78 (12) : 1166 - 1175
  • [39] Accelerated Hot Corrosion Studies of D-Gun-Sprayed Cr2O3-50% Al2O3 Coating on Boiler Steel and Fe-Based Superalloy
    Rani, Amita
    Bala, Niraj
    Gupta, C. M.
    OXIDATION OF METALS, 2017, 88 (5-6): : 621 - 648
  • [40] Wear and corrosion resistance of laser cladding AISI 304 stainless steel/Al2O3 composite coatings
    Xu, Peng
    Lin, ChengXin
    Zhou, ChaoYu
    Yi, XinPeng
    SURFACE & COATINGS TECHNOLOGY, 2014, 238 : 9 - 14
12345