Effect of pre-oxidation on hot corrosion resistance of HR3C stainless steel in sulfate salt with or without Fe2O3

被引：16
|
作者：
Yu, Zheng [1 ]
Lu, Jintao [2 ]
Chen, Minghui [1 ]
Wang, Jinlong [1 ]
Wang, Fuhui [1 ]
机构：
[1] Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China
[2] Xian Thermal Power Res Inst Co Ltd, Xian 710032, Peoples R China
来源：
CORROSION SCIENCE | 2021年 / 192卷
关键词：
Stainless steel; STEM; Hot corrosion; Sulfidation; BEHAVIOR; TECHNOLOGY; PLATELETS; OXYGEN; NI;
D O I：
10.1016/j.corsci.2021.109789
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
HR3C steel exhibits high oxidation resistance in air at 700 degrees C owing to the formation of a dense chmmia scale. In the presence of sulfate salt deposition (Na2SO4:K2SO4 = 1:1), hot corrosion occurs. It leads to the dissolution and re-precipitation of Cr2O3 platelets and severe internal corrosion. Pre-oxidation can notably enhance corrosion resistance with almost no internal corrosion zone. When the deposited sulfate salt contains Fe2O3 (Na2SO4 : K2SO4:Fe2O3 = 1:1:1), HR3C steel suffers even severer hot corrosion. Its scale spalls off easily and internal corrosion develops deep into the steel. Meanwhile, pre-oxidation played almost no positive effect on corrosion in sulfate salt containing Fe2O3.
引用
收藏
页数：9
相关论文
共 50 条
  • [1] Effect of Exposure Temperature on Oxidation of Austenitic Steel HR3C in Supercritical Water
    Zhu, Zhongliang
    Xu, Hong
    Khan, Hasan Izhar
    Jiang, Dongfang
    Zhang, Naiqiang
    OXIDATION OF METALS, 2019, 91 (1-2): : 77 - 93
  • [2] Effect of Pre-Oxidation at 800 A°C on the Pitting Corrosion Resistance of the AISI 316L Stainless Steel
    Buscail, H.
    El Messki, S.
    Riffard, F.
    Perrier, S.
    Issartel, C.
    OXIDATION OF METALS, 2011, 75 (1-2): : 27 - 39
  • [3] Evolution of intergranular corrosion resistance for HR3C heat-resistant austenitic stainless steel at elevated temperature
    Du, H.
    Cheng, Y.
    Hou, L.
    Li, Y.
    Wei, Y.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2017, 52 (05) : 343 - 348
  • [4] Effect of pre-oxidation of Fe3Al on its corrosion resistance in sulfur and chlorine contaminated syngas
    Ilyushechkin, Alexander Y.
    Dolan, Michael D.
    McLennan, Keith G.
    Sharma, Sunil D.
    ASIA-PACIFIC JOURNAL OF CHEMICAL ENGINEERING, 2012, 7 (05) : 716 - 725
  • [5] Corrosion behavior of HR3C austenitic stainless steel in supercritical water near the critical point
    Chen, Hongsheng
    Zhang, Tengfei
    Luo, Jiandong
    Tang, Rui
    Leng, Xuesong
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2023, 74 (09): : 1342 - 1355
  • [6] Effect of Exposure Temperature on Oxidation of Austenitic Steel HR3C in Supercritical Water
    Zhongliang Zhu
    Hong Xu
    Hasan Izhar Khan
    Dongfang Jiang
    Naiqiang Zhang
    Oxidation of Metals, 2019, 91 : 77 - 93
  • [7] Corrosion resistance of HR3C to a carbonate molten salt for energy storage applications in CSP plants
    de Miguel, M. T.
    Encinas-Sanchez, V.
    Lasanta, M. I.
    Garcia-Martin, G.
    Perez, F. J.
    SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2016, 157 : 966 - 972
  • [8] Hot corrosion behaviors of TP347H and HR3C stainless steel with KCl deposit in oxy-biomass combustion
    Zhang, Jiaye
    Rahman, Zia Ur
    Wang, Xuebin
    Wang, Zhao
    Li, Peng
    Wang, Yongbing
    Bate, Delige
    Zhao, Ke
    Tan, Houzhang
    JOURNAL OF ENVIRONMENTAL MANAGEMENT, 2020, 263
  • [9] Fe2O3 films on stainless steel for solar absorbers
    Wu, Sean
    Cheng, Chin-Hsiang
    Hsiao, Yu-Jen
    Juang, Rei-Cheng
    Wen, Wen-Fu
    RENEWABLE & SUSTAINABLE ENERGY REVIEWS, 2016, 58 : 574 - 580
  • [10] Hot-corrosion behavior of HR3C pre-coated alkali metal sulphate in SO2 atmosphere
    Li P.
    Qin P.
    Zhao J.
    Li T.-J.
    Pang S.-J.
    Li, Ping (liping69@dlut.edu.cn), 1600, Beijing Institute of Aeronautical Materials (BIAM) (45): : 43 - 51
12345