Dynamic and static corrosion of alpha-alumina bonded refractory in contact with molten soda-lime-silica (SLS) glass

被引：12

作者：

Wang, Zihua ^{[1
,2
]}

Maotsela, Tlamelo ^{[1
]}

Toperesu, Phillip M. ^{[1
]}

Kale, Girish M. ^{[1
]}

Daji, Jafar ^{[2
]}

Parkinson, David ^{[2
]}

机构：

[1] Univ Leeds, Sch Chem & Proc Engn, Leeds LS2 9JT, W Yorkshire, England

[2] Parkinson Spencer Refractories Ltd, Halifax HX3 6SX, NS, Canada

来源：

CERAMICS INTERNATIONAL | 2019年 / 45卷 / 01期

关键词：

Dynamic corrosion; XRD-SEM-EDS characterisation; Static corrosion; Soda-lime silica glass; High-temperature; Refractories; SYSTEM;

D O I：

10.1016/j.ceramint.2018.09.235

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The corrosion behaviour of sintered high purity alpha-Al2O3 refractory composition in contact with soda-lime-silicate (SLS) glass has been investigated using a dynamic corrosion test designed to simulate industrial conditions. Experiments were conducted as function of rotation speed, contact time duration and temperature. The results of dynamic corrosion tests are in excellent agreement with those obtained from static crucible test at 1370 degrees C for 72 h which is a standard industrial testing practice. The phase composition and microstructures of the glass refractory interface of these samples were studied by X-ray Diffraction (XRD) and combined Scanning Electron Microscopy - Energy Dispersive X-ray Spectroscopy (SEM-EDS), respectively. Elemental mapping was also carried out on the glass-refractory interface.

引用

页码：725 / 732

页数：8

共 20 条

[1] The microstructural features of an alumina-mullite-zirconia refractory material corroded by molten glass [J].

Aksel, C .

CERAMICS INTERNATIONAL, 2003, 29 (03) :305-309

[2] MASS-SPECTROMETRIC AND ELECTROCHEMICAL STUDIES OF THERMODYNAMIC PROPERTIES OF LIQUID AND SOLID-PHASES IN THE SYSTEM CAO-AL2O3 [J].

ALLIBERT, M ;

CHATILLON, C ;

JACOB, KT ;

LOURTAU, R .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (05) :307-314

[3] Corrosion mechanisms of low porosity ZrO2 based materials during near net shape steel casting [J].

Aneziris, CG ;

Pfaff, EM ;

Maier, HR .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2000, 20 (02) :159-168

[4]

[Anonymous], 1973, IRON STEEL ENG

[5]

ASTM, 2009, ANN BOOK ASTM STAND

[6] Dynamic corrosion of Al2O3-ZrO2-SiO2 and Cr2O3-containing refractories by molten frits. Part I: Macroscopic analysis [J].

Baudin, C. ;

Criado, E. ;

Bakali, J. J. ;

Pena, P. .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2011, 31 (05) :697-703

[7] Effect of curing time on the properties of CAC bonded refractory castables [J].

Cardoso, FA ;

Innocentini, MDM ;

Akiyoshi, MM ;

Pandolfelli, VC .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (07) :2073-2078

[8] Role of cement content on the properties of self-flowing Al2O3 refractory castables [J].

Gogtas, Cem ;

Lopez, Hugo F. ;

Sobolev, Konstantin .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2014, 34 (05) :1365-1373

[9] Corrosion resistance of alumina-chromia ceramic materials against molten slag [J].

Hirata, T ;

Morimoto, T ;

Deguchi, A ;

Uchida, N .

MATERIALS TRANSACTIONS, 2002, 43 (10) :2561-2567

[10] POTENTIOMETRIC DETERMINATION OF ACTIVITIES IN THE 2-PHASE FIELDS OF THE SYSTEM NA2O-(ALPHA)AL2O3 [J].

JACOB, KT ;

SWAMINATHAN, K ;

SREEDHARAN, OM .

ELECTROCHIMICA ACTA, 1991, 36 (5-6) :791-798

← 1 2 →