Dry sliding of plasma-sintered iron - The influence of nitriding on wear resistance

被引：13

作者：

Pavanati, H. C. ^{[1
]}

Straffelini, G. ^{[2
]}

Maliska, A. M. ^{[1
]}

Klein, A. N. ^{[1
]}

机构：

[1] Univ Fed Santa Catarina, LABMAT, Dept Engn Mecan, BR-88040970 Florianopolis, SC, Brazil

[2] Univ Trent, Dipartimento Ingn Mat, I-38050 Trento, Italy

来源：

WEAR | 2008年 / 265卷 / 3-4期

关键词：

powder metallurgy; plasma nitriding; confined anode-cathode configuration; chromium enrichment; dry sliding wear resistance;

D O I：

10.1016/j.wear.2007.10.014

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Samples of unalloyed iron were sintered in the presence of an abnormal glow. discharge using the confined anode-cathode configuration in order to allow surface enrichment of the sample with atoms from the cathode. AISI 430 and AISI 1020 cathodes were used to sinter the iron with and without Cr enrichment, respectively. The chromium favors the formation of a hard compound layer after nitriding (with a microhardness up to 1300 HV) due to the presence of chromium nitrides. In order to evaluate the wear resistance and surface damage to the samples, dry sliding wear tests were carried out using a block-on-ring system with applied normal loads of 25-150 N. A large scatter in the experimental results was observed for the unnitrided samples. This effect was attributed to the capacity of the materials to undergo a severe-to-mild wear transition during sliding. Nitriding was found to reduce the wear rate by at least one order of magnitude. In particular, the nitrided samples enriched with chromium (540 degrees C) did not display any damage at 25 N, the lowest normal load used in the present investigation. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：301 / 310

页数：10

共 20 条

[1] Growth of nitrided layers on Fe-Cr alloys [J].

Alves, C ;

Rodrigues, JA ;

Martinelli, AE .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 279 (1-2) :10-15

[2]

Batista VJ, 1998, INT J POWDER METALL, V34, P55

[3]

DANNINGER H, 1993, POWDER METALL INT, V25, P170

[4] Modelling third body flows with a discrete element method- a tool for understanding wear with adhesive particles [J].

Fillot, N. ;

Iordanoff, I. ;

Berthier, Y. .

TRIBOLOGY INTERNATIONAL, 2007, 40 (06) :973-981

[5] 3RD-BODIES IN TRIBOLOGY [J].

GODET, M .

WEAR, 1990, 136 (01) :29-45

[6] ION NITRIDING OF STEELS [J].

JINDAL, PC .

JOURNAL OF VACUUM SCIENCE & TECHNOLOGY, 1978, 15 (02) :313-317

[7] WEAR PROPERTIES OF STEEL PLASMA-NITRIDED AT HIGH-TEMPERATURES [J].

KARAMIS, MB .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 168 (01) :49-53

[8] Severe-mild wear transition by supply of oxide particles on sliding surface [J].

Kato, H .

WEAR, 2003, 255 :426-429

[9] THE UNLUBRICATED WEAR OF SINTERED IRON [J].

LIM, SC ;

BRUNTON, JH .

WEAR, 1986, 113 (03) :371-382

[10]

LOURENCO JM, 2004, MAT RES, V7, P267

← 1 2 →