Cement paste characteristics and porous concrete properties

被引：230

作者：

Chindaprasirt, P. ^{[1
]}

Hatanaka, S. ^{[2
]}

Chareerat, T. ^{[1
]}

Mishima, N. ^{[2
]}

Yuasa, Y. ^{[3
]}

机构：

[1] Khon Kaen Univ, Dept Civil Engn, Khon Kaen 40002, Thailand

[2] Mie Univ, Fac Engn, Dept Architecture, Tsu, Mie, Japan

[3] Mie Prefecture Sci & Technol Promot Ctr, Ind Res Div, Tsu, Mie, Japan

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2008年 / 22卷 / 05期

关键词：

cement paste; porous concrete; compressive strength; void ratio; compaction;

D O I：

10.1016/j.conbuildmat.2006.12.007

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In this paper, cement paste characteristics and porous concrete properties are studied. The results indicate that cement paste characteristics are dependent on the water to cement ratio (W/C), admixture and mixing time. Cement paste with high viscosity and high flow suitable for making porous concrete is obtained with the use of low W/C of 0.20-0.25, an incorporation of 1% superplasticizer, and sufficient mixing. Porous concretes having suitable void ratios are produced with appropriate paste content and flow, and sufficient compaction. Good porous concretes with void ratio of 15-25% and strength of 22-39 MPa are produced using paste with flow of 150-230 mm and top surface vibration of 10 s with vibrating energy of 90 kN m/m(2). For low void ratio, high strength porous concrete of 39 MPa is obtained using paste with low flow. For high void ratio, porous concrete of 22 MPa is obtained using paste with high flow. Furthermore, the results indicate that the strength of porous concrete could be estimated from strength equation of porous brittle material. (C) 2007 Elsevier Ltd. All rights reserved.

引用

页码：894 / 901

页数：8

共 26 条

[11]

*JIS, A5001 JIS

[12]

*JIS, R5201 JIS

[13]

Malhotra V.M., 1976, J. Proc., V73, P628

[14]

Meininger R.C., 1988, Concr. Int., V10, P20

[15]

MISHIMA N, 2000, J STRUCT CONSTRUCT E, P528

[16] COMPRESSION STRENGTH OF POROUS SINTERED ALUMINA AND ZIRCONIA .9. TO CERAMOGRAPHY [J].

RYSHKEWITCH, E .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1953, 36 (02) :65-68

[17]

SCHAEFER VR, 2006, DESIGN DEV PREVIOUS, P85

[18]

SOEDA M, 1998, P JAPAN CONCRETE I, V20

[19]

TAMAI M, 2000, CURRENT STATE PROSPE, P6

[20]

TAMAI M, 1988, P PAC CONCR C, V2, P463

← 1 2 3 →