Synergistic effects of deposits and sulfate reducing bacteria on the corrosion of carbon steel

被引：67
|
作者：
Yang, J. [1 ,2 ]
Wang, Z. B. [1 ]
Qiao, Y. X. [3 ]
Zheng, Y. G. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
[3] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 199卷
关键词：
Carbon steel; Under-deposit corrosion; Microbiologically influenced corrosion; Sulfate reducing bacteria; Synergistic effect; MICROBIOLOGICALLY INFLUENCED CORROSION; OIL; IRON; BEHAVIOR; ENVIRONMENT; INHIBITORS; MECHANISM; PIPELINES; SEAWATER; CHLORIDE;
D O I：
10.1016/j.corsci.2022.110210
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The synergistic effects of deposits and sulfate reducing bacteria (SRB) on the corrosion of a carbon steel are clarified by purposely designing four groups of experiments. The weight loss combined with electrochemical measurements and the surface profiling determine quantitatively that deposits and SRB contribute synergistically similar to 75% and similar to 49% to uniform and localized corrosion, respectively. Based on the experimental evidence, the synergism is explained in terms of the promotion effects of SRB on under-deposit corrosion (UDC) due to unevenly distributed iron sulfides produced by SRB and the acceleration effects of deposits on SRB corrosion resulting from UDC-induced accumulation of SRB.
引用
收藏
页数：11
相关论文
共 50 条
  • [11] Method for studying stabilization of localized corrosion on carbon steel by sulfate-reducing bacteria
    Campaignolle, X
    Crolet, JL
    CORROSION, 1997, 53 (06) : 440 - 447
  • [12] The synergistic effect of parallel magnetic field and sulfate-reducing bacteria on stress corrosion cracking of buried X80 pipeline steel
    Wang, Yuxin
    He, Jianyu
    Xie, Fei
    Zhang, Ying
    Wang, Guofu
    Sun, Dongxu
    Wang, Dan
    Wu, Ming
    Qin, Yue
    Jia, Wenlong
    ENGINEERING FAILURE ANALYSIS, 2023, 154
  • [13] Corrosion of 907 Steel Influenced by Sulfate-Reducing Bacteria
    Chen, Juna
    Wu, Jiajia
    Wang, Peng
    Zhang, Dun
    Chen, Shiqiang
    Tan, Faqi
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (03) : 1469 - 1479
  • [14] Effect of test media on the crevice corrosion of stainless steel by sulfate reducing bacteria
    Javed, M. A.
    Neil, W. C.
    Wade, S. A.
    NPJ MATERIALS DEGRADATION, 2022, 6 (01)
  • [15] Effects of sulfate-reducing bacteria on the corrosion behavior of carbon steel
    Kuang, Fei
    Wang, Jia
    Yan, Li
    Zhang, Dun
    ELECTROCHIMICA ACTA, 2007, 52 (20) : 6084 - 6088
  • [16] Synergistic Effect of Iron Bacteria and Vibrio on Carbon Steel Corrosion in Seawater
    Ke, Rui
    Chai, Ke
    Wu, Jinyi
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2016, 11 (09): : 7461 - 7474
  • [17] Microbial corrosion of initial perforation on abandoned pipelines in wet soil containing sulfate-reducing bacteria
    Liu, Hongwei
    Cheng, Y. Frank
    COLLOIDS AND SURFACES B-BIOINTERFACES, 2020, 190
  • [18] Understanding the corrosion of pipe steel due to the adhesion of sulfate reducing bacteria film combined with the deposit layer
    Xu, Huatian
    Gao, Kewei
    Xiong, Qi
    Li, Haonan
    Zhong, Xiankang
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2023, 37 (15) : 2247 - 2260
  • [19] Corrosion behavior of carbon steel in the presence of sulfate reducing bacteria and iron oxidizing bacteria cultured in oilfield produced water
    Liu, Hongwei
    Fu, Chaoyang
    Gu, Tingyue
    Zhang, Guoan
    Lv, Yalin
    Wang, Haitao
    Liu, Hongfang
    CORROSION SCIENCE, 2015, 100 : 484 - 495
  • [20] Effect of sulfate-reducing bacteria on hydrogen permeation and stress corrosion cracking behavior of 980 high-strength steel in seawater
    Lv, Meiying
    Chen, Xuchao
    Li, Zhenxin
    Du, Min
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 92 : 109 - 119
12345