Improving welding stresses by filler metal and heat control selection in component-related butt joints of high-strength steel

被引：14
作者：
Schroepfer, Dirk [1 ]
Kromm, Arne [1 ]
Kannengiesser, Thomas [1 ]
机构：
[1] BAM Fed Inst Mat Res & Testing, Berlin, Germany
来源：
WELDING IN THE WORLD | 2015年 / 59卷 / 03期
关键词：
Residual stresses; MAG welding; Restraint; High-strength steels; Process parameters; RESIDUAL-STRESSES;
D O I：
10.1007/s40194-014-0219-7
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The application of high-strength fine-grained structural steels with yield strengths greater than or equal to 690 MPa expands because of present light weight design trends. The requirements regarding the welded components safety increased due to high loading capacity. This determines a sustainable and economic application as well. However, high welding residual stresses could diminish the components safety, especially due to high restraint conditions in component or repair welds. Therefore, this work is concerned with global and local welding stresses, especially crack-critical welding stresses in the HAZ and while root welding due to the restraint conditions. Restraint intensities of real components were analysed and realised with two different weld tests, alongside two different plate dimensions and steel grades. A comparison of the test results showed several significant effects for heat control and restraint intensity regarding restraint forces and local welding stresses. Among these effects, substantial influences were found for the filler metal selection with partially altered results for root and filler beads. Local stresses of weld seam and HAZ were affected differently.
引用
收藏
页码：455 / 464
页数：10
相关论文
共 29 条
  • [1] Alexandrov B.T., 2007, Welding in the World, V51, P48
  • [2] [Anonymous], 2011, 14341 EN ISO
  • [3] [Anonymous], 2001, 10112 DIN EN
  • [4] [Anonymous], 2011, 100256 EN
  • [5] Bhadeshia H. K. D. H., 1995, Mathematical modelling of weld phenomena, P71
  • [6] Developments in martensitic and bainitic steels: role of the shape deformation
    Bhadeshia, HKDH
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 378 (1-2): : 34 - 39
  • [7] Boellinghaus T, 2003, TRENDS IN WELDING RESEARCH, PROCEEDINGS, P906
  • [8] Bollinghaus T, 2005, MATH MODELLING WELD, V7, P651
  • [9] Characterizing Phase Transformations and Their Effects on Ferritic Weld Residual Stresses with X-Rays and Neutrons
    Dai, H.
    Francis, J. A.
    Stone, H. J.
    Bhadeshia, H. K. D. H.
    Withers, P. J.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (13): : 3070 - 3078
  • [10] EN, 1993, EUR 3 DES STEEL STRU
123