CORROSION INHIBITION OF MOLYBDATE AND NITRITE FOR CARBON STEEL CORROSION IN PROCESS COOLING WATER

被引：0

作者：

Yee, J. C. ^{[1
]}

Kee, K. E. ^{[1
]}

Hassan, Suhaimi ^{[1
]}

Nor, M. Faizairi M. ^{[1
]}

Ismail, M. C. ^{[1
]}

机构：

[1] Univ Teknol Petronas, Ctr Corros Res, Dept Mech Engn, Seri Iskandar 32610, Perak, Malaysia

来源：

JOURNAL OF ENGINEERING SCIENCE AND TECHNOLOGY | 2019年 / 14卷 / 04期

关键词：

Cooling water; Corrosion inhibitor; Molybdate; Nitrite; Process; MILD-STEEL; SODIUM MOLYBDATE; NATURAL-WATERS; ANIONS; ACID;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Process cooling water systems require effective chemical treatment to protect steel pipelines against corrosion attack. In this work, experiments were conducted to study the inhibition effect of molybdate and nitrite on the corrosion of carbon steel in the presence of open recirculating flow condition. Carbon steel grade 1018 was used as specimens by way of immersion test in a Simulated Cooling Water (SCW) solution, within a rotating cage and mini flow circuit experiments. Corrosion rates were measured by weight loss method after immersion for 72 hours. Results showed that the combined inhibitor treatment of molybdate and nitrite showed a synergistic effect in reducing the corrosion rate to less than 0.01 mm/y with the inhibition efficiency of 99.6%. The rotating cage results showed good correlation with mini flow circuit results. Surface morphology showed that inhibited steel was protected by oxide film but still suffered some pitting.

引用

页码：2431 / 2444

页数：14

共 27 条

[1] Effect of anions on the efficiency of aromatic carboxylic acid corrosion inhibitors in near neutral media: Experimental investigation and theoretical modeling [J].

Agarwal, P ;

Landolt, D .

CORROSION SCIENCE, 1998, 40 (4-5) :673-691

[2] TREATMENT OF WASTEWATER TO MEET THE REQUIREMENTS FOR COOLING WATER SYSTEMS IN JORDAN'S NUCLEAR PLANTS [J].

Al-Rawajfeh, Aiman Eid ;

Araj, Kamal .

CHEMICAL AND PROCESS ENGINEERING-INZYNIERIA CHEMICZNA I PROCESOWA, 2013, 34 (02) :253-267

[3]

Ali M.R., 2009, J. Sci. Res., V1, P82

[4]

[Anonymous], 2004, G3172 ASTM

[5]

Aquaprox, 2009, TREATM COOL WAT

[6] Effects of Solution Hydrodynamics on Corrosion Inhibition of Steel by Citric Acid in Cooling Water [J].

Ashassi-Sorkhabi, H. ;

Asghari, E. ;

Mohammadi, M. .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (08) :2992-3000

[7]

ASTM International, 2012, G18406 ASTM INT

[8]

ASTM International, 2015, D268815E1 ASTM INT

[9] Corrosion management in power plant cooling systems using tertiary-treated municipal wastewater as makeup water [J].

Choudhury, Mahbuboor R. ;

Hsieh, Ming-Kai ;

Vidic, Radisav D. ;

Dzombak, David A. .

CORROSION SCIENCE, 2012, 61 :231-241

[10] Inhibition Effect of Environment-Friendly Inhibitors on the Corrosion of Carbon Steel in Recirculating Cooling Water [J].

He, Chengjun ;

Tian, Zhipeng ;

Zhang, Bingru ;

Lin, Yu ;

Chen, Xi ;

Wang, Meijing ;

Li, Fengting .

INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2015, 54 (07) :1971-1981

← 1 2 3 →