Finite element and experimental investigation on the effects of temperature, strain and strain rate on microstructure and mechanical properties of FSSWed TRIP steel joints

被引:7
作者
Ebrahimpour, Ali [1 ]
Mostafapour, Amir [2 ]
Samadian, Kaveh [3 ]
机构
[1] Univ Tabriz, Mianeh Tech & Engn Fac, Tabriz, Iran
[2] Univ Tabriz, Fac Mech Engn, Tabriz, Iran
[3] Univ Ghent, Labo Soete, Dept Elect Energy Met Mech Construct & Syst, Ghent, Belgium
关键词
finite element modeling; friction stir spot welding; TRIP steel; microstructure; MICROALLOYED STEELS; RETAINED AUSTENITE; ASSISTED STEELS; LOW-ALLOY; RECRYSTALLIZATION; PARAMETERS; SIZE;
D O I
10.1088/2053-1591/aae8f3
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
FSSWed TRIP steel joints were investigated at four rotational speed of 900, 1200, 1500 and 1800 rpm. A finite element model was developed to obtain thermal history, strain and strain rate during welding and the results validated by experimental data. The microstructure, microhardness distribution and shear tensile strength were examined. The FSSW process successfully produced high integrity completely defect-free joints at all the proposed welding parameters. As a result of temperature and strain distribution imposed by process, three different zones were determined in welding region: stir zone with recrystallized structure, thermomechanical affected zone with major phase of martensite and heat affected zones. The maximum microhardnees was achieved at stir zone and decreased by getting away from keyhole. Totally the microhardness increased by increasing rotational speed. It was obtained that the strength of joints increased to a maximum value of 9.9 kN in 1500 rpm and then decreases to 8.4 kN at 1800 rpm. By increasing rotational speed, the strain rate increased and causes to recrystallization of the prior austenite grains, but in high rotational speed, the higher temperature causes to grain growth in recrystallized grains. The fracture surfaces of joints showed a dimple pattern ductile fracture in all cases except 1800 rpm that the fracture was less ductile which agrees with lower tensile elongation of it.
引用
收藏
页数:12
相关论文
共 27 条
[1]   Microstructure and mechanical properties evolution of friction stir spot welded high-Mn twinning-induced plasticity steel [J].
Ahmed, M. M. Z. ;
Ahmed, Essam ;
Hamada, A. S. ;
Khodir, S. A. ;
Seleman, M. M. El-Sayed ;
Wynne, B. P. .
MATERIALS & DESIGN, 2016, 91 :378-387
[2]  
[Anonymous], 2002, PHYS METALLURGY HDB
[3]   Strains and strain rates during friction stir welding [J].
Arora, A. ;
Zhang, Z. ;
De, A. ;
DebRoy, T. .
SCRIPTA MATERIALIA, 2009, 61 (09) :863-866
[4]   Influence of rolling of TRIP steel in the intercritical region on the stability of retained austenite [J].
Basuki, A ;
Aernoudt, E .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1999, 90 :37-43
[5]  
Bhadeshia H.K. D. H., 1997, Mathematical Modelling of Weld Phenomena-3, P229
[6]   Strain and strain rate during friction stir welding/processing of Al-7Si-0.3Mg alloy [J].
Chen, Z. W. ;
Cui, S. .
PROCESSING, MICROSTRUCTURE AND PERFORMANCE OF MATERIALS, 2009, 4
[7]   Superplastic Forming of Friction Stir Welded AA6061-T6 Alloy Sheet with Various Tool Rotation Speed [J].
Ganesh, P. ;
Kumar, V. S. Senthil .
MATERIALS AND MANUFACTURING PROCESSES, 2015, 30 (09) :1080-1089
[8]   Metallographic methods for revealing the multiphase microstructure of TRIP-assisted steels [J].
Girault, E ;
Jacques, P ;
Harlet, P ;
Mols, K ;
Van Humbeeck, J ;
Aernoudt, E ;
Delannay, F .
MATERIALS CHARACTERIZATION, 1998, 40 (02) :111-118
[9]   Microstructure and mechanical properties of friction stir processed AISI 316L stainless steel [J].
Hajian, M. ;
Abdollah-zadeh, A. ;
Rezaei-Nejad, S. S. ;
Assadi, H. ;
Hadavi, S. M. M. ;
Chung, K. ;
Shokouhimehr, M. .
MATERIALS & DESIGN, 2015, 67 :82-94
[10]   A review of numerical analysis of friction stir welding [J].
He, Xiaocong ;
Gu, Fengshou ;
Ball, Andrew .
PROGRESS IN MATERIALS SCIENCE, 2014, 65 :1-66