Characterization of protective coatings for planar automotive gas sensors

Alumina support material suitable for use as a planar automotive gas sensor support was coated in thin films of yttria-stabilised zirconia (YSZ) and titania. The morphology, composition, thickness and homogeneity of the coating was measured. The coating was applied to the 'green' form of a tape cast alumina substrate which was subsequently fired at 1500 degrees C to produce the final form of the coated alumina. The YSZ coating gave a continuous similar to 5 mu m thick coating with no evidence of mixed oxide formation between the YSZ and the alumina substrate. XRD indicated a face centred cubic Y doped ZrO2 or primitive tetragonal Zr0.9Y0.1O1.95 phase. The titania coatings were much thinner (<1 mu m) with signs of trace amounts of aluminum titanium oxide (Al2TiO5) as well as rutile titania in XRD. Spot analysis using X-ray photoelectron spectroscopy showed a fairly regular titania coverage. Atomic force microscopy analysis showed a particle size of 1-3 mu m for the YSZ coating and similar to 0.5 mu m for titania. (C) 2005 Elsevier B.V. All rights reserved.