High-Strength Geopolymer Using Fine High-Calcium Fly Ash

被引：242

作者：

Chindaprasirt, P. ^{[1
]}

Chareerat, T. ^{[2
]}

Hatanaka, S. ^{[3
]}

Cao, T.

机构：

[1] Khon Kaen Univ, Sustainable Infrastruct Res & Dev Ctr, Dept Civil Engn, Fac Engn, Khon Kaen 40002, Thailand

[2] Ubon Ratchathani Univ, Fac Engn, Dept Civil Engn, Ubon Ratchathani 34190, Thailand

[3] Mie Univ, Dept Architecture, Tsu, Mie 5148507, Japan

来源：

JOURNAL OF MATERIALS IN CIVIL ENGINEERING | 2011年 / 23卷 / 03期

关键词：

Geopolymer; Fly-ash fineness; Flow; High strength; Drying shrinkage; CEMENT; RESISTANCE; MICROSTRUCTURE; TEMPERATURE; WORKABILITY;

D O I：

10.1061/(ASCE)MT.1943-5533.0000161

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In this paper, the synthesis of high-strength geopolymer using fine high-calcium fly ash was studied. The effect of fineness of fly ash on the setting time of geopolymer paste, workability, strength development, and drying shrinkage of geopolymer mortars made from classified fine high-calcium fly ash was investigated. Air-classified fly ash with three different finenesses coarse original fly ash (CFA), medium-fineness fly ash (MFA), and fine fly ash (FFA) from the Mae Moh Power Station was used for this study. The heat-cured geopolymers were activated with sodium hydroxide (NaOH) and sodium silicate. A small amount of water was incorporated for workability. The results indicate that the setting time of paste decreases with an increase in fly-ash fineness. The flow, strength, and drying-shrinkage characteristics of mortars were improved using fine fly ash. Geopolymer mortars with high 28-day compressive strength of 86.0 MPa were obtained. DOI: 10.1061/(ASCE)MT.1943-5533.0000161. (C) 2011 American Society of Civil Engineers.

引用

页码：264 / 270

页数：7

共 46 条

[1]

Adams S, 2019, ANN ONCOL, V30, P397, DOI [10.1093/annonc/mdy518, 10.1093/annonc/mdy517]

[2]

[Anonymous], C18809 ASTM

[3]

[Anonymous], 2009, C59609 ASTM

[4]

ASTM, 2007, C143707 ASTM