Oxidation of SiC/BN/SiC ceramic matrix composites in dry and wet oxygen at intermediate temperatures

The oxidation behavior of SiC/BN/SiC ceramic matrix composites (CMCs) was evaluated from 400? to 800 ?C in 100% O-2 and 50% H2O/50% O-2 gas mixtures. Thermogravimetric analysis (TGA) was utilized to measure weight change during controlled environment exposures at elevated temperatures for 1 and 50 hours. Oxidized CMCs and their oxides were studied post-exposure with scanning electron microscopy and energy dispersive spectroscopy. The oxidation onset and composition transition temperatures were evaluated. Key observations include oxide composition, oxide wetting, oxygen solubility in Hi-Nicalon SiC fibers and BN fiber coating oxidation and volatility behavior as a function of temperature. Degradation in wet environments at 600 ?C was most extensive due to the formation of a non-wetting, non-protective surface oxide, allowing oxidant access to the BN fiber coatings followed by oxidation and volatilization. Implications of the CMC oxidation behavior are discussed for CMCs in service.