Filiform corrosion of aluminium sheet. II. Electrochemical and corrosion behaviour of rare substrates

被引:61
作者
Leth-Olsen, H [1 ]
Afseth, A [1 ]
Nisancioglu, K [1 ]
机构
[1] Norwegian Univ Sci & Technol, Dept Electrochem, N-7034 Trondheim, Norway
关键词
aluminium; filiform; corrosion;
D O I
10.1016/S0010-938X(98)00025-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Coiled rolled aluminium substrates of the AA1000, 3000 and 5000 series in various tempers were characterized by corrosion potential (E-corr) and porentiostatic measurements in an acidic chloride solution. The time dependence of these data indicated the presence of an active surface layer on the annealed substrates that were susceptible to filiform corrosion (FFC) after painting. This layer was electrochemically more active than the bulk of the material whose E-corr was stable at the well known critical pitting potential (E-c) of the alloy. The E-corr of an active substrate was more negative than the E-c of the bulk rnetal immediately after exposure to the test solution. rising to the bulk E-c with immersion time, as the active layer dissolved in the solution. Analogously, potentiostatic measurements at E-c indicated high anodic current transients, decaying with time to lower steady-state values after an equivalent amount of metal (of the order 1 mu m in thickness) was removed from the surface. The reactivity of the layers, quantified in this manner, depended on the chemical composition of the substrates in the same way as the susceptibility of the layers to FFC. (C) 1998 Elsevier Science Ltd. All rights reserved
引用
收藏
页码:1195 / 1214
页数:20
相关论文
共 50 条
[41]   Corrosion behaviour of the microbially modified surface of 5083 aluminium alloy [J].
Nkoua, C. ;
Josse, C. ;
Proietti, A. ;
Basseguy, R. ;
Blanc, C. .
CORROSION SCIENCE, 2023, 210
[42]   The Effect of Cold Rolling on the Corrosion Behaviour of 5083 Aluminium Alloys [J].
Panagopoulos, C. N. ;
Georgiou, E. P. .
METALS, 2024, 14 (02)
[43]   AC Corrosion behaviour of aluminium and zinc sacrificial anodes in seawater [J].
Tian, Nianpei ;
Du, Yanxia ;
Liang, Yi ;
Yuan, Xun ;
Chen, Le .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2022, 57 (02) :169-177
[44]   Corrosion behaviour of aluminium in rain water containing garlic extract [J].
Priya, SL ;
Chitra, A ;
Rajendran, S ;
Anuradha, K .
SURFACE ENGINEERING, 2005, 21 (03) :229-231
[45]   Inhibitive Behaviour of Corrosion of Aluminium Alloy in NaCl by Mangrove Tannin [J].
Yahya, Solhan ;
Rahim, Afidah Abdul ;
Shah, Affaizza Mohd ;
Adnan, Rohana .
SAINS MALAYSIANA, 2011, 40 (09) :953-957
[46]   Corrosion behaviour of aluminium-magnesium alloys in molten sodium [J].
Li, XJ ;
Rao, X ;
Zhang, D ;
Si, PC .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2000, 10 (02) :224-227
[47]   The cathodic corrosion of aluminium during the electrodeposition of paint: Electrochemical measurements [J].
Hulser, P ;
Kruger, UA ;
Beck, F .
CORROSION SCIENCE, 1996, 38 (01) :47-57
[49]   Electrochemical study on corrosion behaviour of steels in sand with water [J].
Wang Jia .
Chinese Journal of Oceanology and Limnology, 1997, 15 (4) :369-372
[50]   An electrochemical study of the corrosion behaviour of metals in canola biodiesel [J].
Rocabruno-Valdes, C. I. ;
Hernandez, J. A. ;
Juantorena, A. U. ;
Arenas, E. G. ;
Lopez-Sesenes, R. ;
Salinas-Bravo, V. M. ;
Gonzalez-Rodriguez, J. G. .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2018, 53 (02) :153-162