Influence of Hydrostatic Pressure on the Pitting Corrosion Behavior of API X80 Steel

被引：0
作者：
Xu, Chengcheng [1 ]
Yu, Meng [1 ]
Zhu, Yuxiang [1 ]
Jin, Ying [1 ]
Wen, Lei [1 ]
Sun, Dongbai [2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Sun Yat Sen Univ, Sch Mat, Guangzhou 510275, Peoples R China
来源：
CORROSION | 2021年 / 77卷 / 12期
关键词：
hydrostatic pressure; inclusions; pitting corrosion; X80; steel; 316L STAINLESS-STEEL; CARBON-STEEL; PIPELINE STEEL; ALUMINUM; POLARIZATION; TEMPERATURE; BICARBONATE; INITIATION; STRESS; NICKEL;
D O I：
10.5006/3810
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of hydrostatic pressure on the metastable and stable pitting corrosion of API X80 steel was investigated in a simulated deep-sea environment. Cumulative probability distribution analysis of metastable pitting events revealed that hydrostatic pressure promoted the occurrence of metastable pitting corrosion and the transformation of metastable pitting corrosion to stable pitting corrosion. According to the results of scanning Kelvin probe force microscopy tests, pitting corrosion of the test steel originated at the interface between inclusions and the substrate. Combined with finite element analysis, the mechanism by which hydrostatic pressure promoted the occurrence and propagation of stable pitting corrosion of test steel in the simulated deep-sea environment was explained.
引用
收藏
页码：1299 / 1310
页数：12
相关论文
共 50 条
[41]   Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment [J].
Li, Zhong ;
Li, Caiyu ;
Qian, Hongchang ;
Li, Jun ;
Huang, Liang ;
Du, Cuiwei .
MATERIALS, 2017, 10 (07)
[42]   Effect of alternating current frequency on corrosion behavior of X80 pipeline steel in soil extract solution of Dagang [J].
Qin, Qingyu ;
Wei, Boxin ;
Bai, Yunlong ;
Nan, Li ;
Xu, Jin ;
Yu, Changkun ;
Sun, Cheng .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2020, 179
[43]   Effect of hydrostatic pressure on the pitting corrosion of 17-4PH martensitic stainless steel [J].
Ma, Hongyu ;
Liu, Rui ;
Ke, Peiling ;
Cui, Yu ;
Liu, Li ;
Wang, Fuhui .
ENGINEERING FAILURE ANALYSIS, 2022, 138
[44]   Hydrostatic pressure effects on corrosion behavior of X70 pipeline steel in a simulated deep-sea environment [J].
Yang, Z. X. ;
Kan, B. ;
Li, J. X. ;
Su, Y. J. ;
Qiao, L. J. .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2018, 822 :123-133
[45]   Study on corrosion behavior of X80 steel under stripping coating by sulfate reducing bacteria [J].
Cui, Yan-Yu ;
Qin, Yong-Xiang ;
Ding, Qing-Miao ;
Gao, Yu-Ning .
BMC BIOTECHNOLOGY, 2021, 21 (01)
[46]   Effect of magnetic field on the electrochemical corrosion behavior of X80 pipeline steel [J].
Wang, Dan ;
Li, Tianjiao ;
Xie, Fei ;
Wang, Yue ;
Wang, Haoqian .
CONSTRUCTION AND BUILDING MATERIALS, 2022, 350
[47]   Passivity and Pitting Corrosion of X80 Pipeline Steel in Carbonate/Bicarbonate Solution Studied by Electrochemical Measurements [J].
H. B. Xue ;
Y. F. Cheng .
Journal of Materials Engineering and Performance, 2010, 19 :1311-1317
[48]   Hydrogen Permeation and Electrochemical Corrosion Behavior of the X80 Pipeline Steel Weld [J].
Xue, H. B. ;
Cheng, Y. F. .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (01) :170-175
[49]   Corrosion Behavior of X80 Steel under Dynamic DC Interference and SRB [J].
Zhang H. ;
Gao B.-W. ;
Yan M.-C. ;
Li D.-B. ;
Xu Y.-N. .
Surface Technology, 2022, 51 (08) :330-341
[50]   Influence of riboflavin on the corrosion of X80 pipeline steel by Sulfate reducing bacteria [J].
Fu, Lei ;
Jian, Ke ;
Lin, Li ;
Wang, Zhengguo ;
Yang, Hang ;
Luo, Yunrong ;
Yan, Shisen ;
Zhu, Daqian .
MATERIALS RESEARCH EXPRESS, 2024, 11 (07)
12345