Influence of Hydrostatic Pressure on the Pitting Corrosion Behavior of API X80 Steel

被引：0

作者：

Xu, Chengcheng ^{[1
]}

Yu, Meng ^{[1
]}

Zhu, Yuxiang ^{[1
]}

Jin, Ying ^{[1
]}

Wen, Lei ^{[1
]}

Sun, Dongbai ^{[2
]}

机构：

[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China

[2] Sun Yat Sen Univ, Sch Mat, Guangzhou 510275, Peoples R China

来源：

CORROSION | 2021年 / 77卷 / 12期

关键词：

hydrostatic pressure; inclusions; pitting corrosion; X80; steel; 316L STAINLESS-STEEL; CARBON-STEEL; PIPELINE STEEL; ALUMINUM; POLARIZATION; TEMPERATURE; BICARBONATE; INITIATION; STRESS; NICKEL;

D O I：

10.5006/3810

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of hydrostatic pressure on the metastable and stable pitting corrosion of API X80 steel was investigated in a simulated deep-sea environment. Cumulative probability distribution analysis of metastable pitting events revealed that hydrostatic pressure promoted the occurrence of metastable pitting corrosion and the transformation of metastable pitting corrosion to stable pitting corrosion. According to the results of scanning Kelvin probe force microscopy tests, pitting corrosion of the test steel originated at the interface between inclusions and the substrate. Combined with finite element analysis, the mechanism by which hydrostatic pressure promoted the occurrence and propagation of stable pitting corrosion of test steel in the simulated deep-sea environment was explained.

引用

页码：1299 / 1310

页数：12

共 58 条

[21] Metastable pitting characteristics of aluminium alloys measured using current transients during potentiostatic polarisation [J].

Gupta, R. K. ;

Sukiman, N. L. ;

Cavanaugh, M. K. ;

Hinton, B. R. W. ;

Hutchinson, C. R. ;

Birbilis, N. .

ELECTROCHIMICA ACTA, 2012, 66 :245-254

[22]

Gutman E.M., 1994, MECHANOCHEMISTRY SOL, P18

[23] The mechanochemical behavior of type 316L stainless steel [J].

Gutman, EM ;

Solovioff, G ;

Eliezer, D .

CORROSION SCIENCE, 1996, 38 (07) :1141-1145

[24] Influence of hydrostatic pressure on the corrosion behavior of 90/10 copper-nickel alloy tube under alternating dry and wet condition [J].

Hu, Shengbo ;

Liu, Li ;

Cui, Yu ;

Li, Ying ;

Wang, Fuhui .

CORROSION SCIENCE, 2019, 146 :202-212

[25] An induced corrosion inhibition of X80 steel by using marine bacterium Marinobacter salsuginis [J].

Khan, M. Saleem ;

Yang, Chunguang ;

Zhao, Ying ;

Pan, Haobo ;

Zhao, Jinlong ;

Shahzad, M. Babar ;

Kolawole, Sharafadeen Kunle ;

Ullah, Ihsan ;

Yang, Ke .

COLLOIDS AND SURFACES B-BIOINTERFACES, 2020, 189

[26] Insights on the Al-Cu-Fe-Mn intermetallic particles induced pitting corrosion of Al-Cu-Li alloy [J].

Li, Meicheng ;

Seyeux, Antoine ;

Wiame, Frederic ;

Marcus, Philippe ;

Swiatowska, Jolanta .

CORROSION SCIENCE, 2020, 176

[27] Effect of Deep Sea Pressures on the Corrosion Behavior of X65 Steel in the Artificial Seawater [J].

Li, Qiu-Shi ;

Luo, Shun-Zhong ;

Xing, Xu-Teng ;

Yuan, Jing ;

Liu, Xin ;

Wang, Ji-Hui ;

Hu, Wen-Bin .

ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2019, 32 (08) :972-980

[28] Synergistic effect of chloride ion and Shewanella algae accelerates the corrosion of Ti-6Al-4V alloy [J].

Li, Zhong ;

Wang, Jie ;

Dong, Yizhe ;

Xu, Dake ;

Zhang, Xianhui ;

Wu, Jianhua ;

Gu, Tingyue ;

Wang, Fuhui .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 71 :177-185

[29] Multi-phase-field modeling of localized corrosion involving galvanic pitting and mechano-electrochemical coupling [J].

Lin, Chen ;

Ruan, Haihui .

CORROSION SCIENCE, 2020, 177

[30] Synergistic Effect of Al2O3 Inclusion and Pearlite on the Localized Corrosion Evolution Process of Carbon Steel in Marine Environment [J].

Liu, Chao ;

Cheng, Xuequn ;

Dai, Zeyu ;

Liu, Ryan ;

Li, Ziyu ;

Cui, Liying ;

Chen, Mindong ;

Ke, Le .

MATERIALS, 2018, 11 (11)

← 1 2 3 4 5 6 →