Influence of Hydrostatic Pressure on the Pitting Corrosion Behavior of API X80 Steel

被引：0
|
作者：
Xu, Chengcheng [1 ]
Yu, Meng [1 ]
Zhu, Yuxiang [1 ]
Jin, Ying [1 ]
Wen, Lei [1 ]
Sun, Dongbai [2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Sun Yat Sen Univ, Sch Mat, Guangzhou 510275, Peoples R China
来源：
CORROSION | 2021年 / 77卷 / 12期
关键词：
hydrostatic pressure; inclusions; pitting corrosion; X80; steel; 316L STAINLESS-STEEL; CARBON-STEEL; PIPELINE STEEL; ALUMINUM; POLARIZATION; TEMPERATURE; BICARBONATE; INITIATION; STRESS; NICKEL;
D O I：
10.5006/3810
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of hydrostatic pressure on the metastable and stable pitting corrosion of API X80 steel was investigated in a simulated deep-sea environment. Cumulative probability distribution analysis of metastable pitting events revealed that hydrostatic pressure promoted the occurrence of metastable pitting corrosion and the transformation of metastable pitting corrosion to stable pitting corrosion. According to the results of scanning Kelvin probe force microscopy tests, pitting corrosion of the test steel originated at the interface between inclusions and the substrate. Combined with finite element analysis, the mechanism by which hydrostatic pressure promoted the occurrence and propagation of stable pitting corrosion of test steel in the simulated deep-sea environment was explained.
引用
收藏
页码：1299 / 1310
页数：12
相关论文
共 50 条
  • [1] Hydrostatic pressure effects on corrosion behaviour of X80 steel in artificial sea water
    Xu, Chengcheng
    Zhu, Yuxiang
    Liu, Wanlei
    Bao, Feihu
    Liu, Erju
    Huang, Feifei
    Wen, Lei
    Jie, Ying
    Sun, Dongbai
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2021, 56 (04) : 383 - 391
  • [2] Influence of Hydrostatic Pressure on Corrosion Behavior of Cerium Conversion Coating on X80
    Qu Shaopeng
    Li Chao
    Dong Lihua
    Yin Yansheng
    Yang Lijing
    CHINA SURFACE ENGINEERING, 2019, 32 (05) : 95 - 102
  • [3] Effect of Temperature on the Corrosion Behavior of API X80 Steel Pipeline
    Paul, Okonkwo C.
    Ahmed, Essam
    Mohamed, A. M. A.
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2015, 10 (12): : 10246 - 10260
  • [4] Influence of Temperature on the Corrosion Behavior of X80 Steel in an Acidic Soil Environment
    Wu, Yuanhui
    Luo, Suxing
    Mou, Qingsong
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01): : 576 - 586
  • [5] A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel
    Yang, Zixuan
    Kan, Bo
    Li, Jinxu
    Su, Yanjing
    Qiao, Lijie
    Volinsky, Alex A.
    MATERIALS, 2017, 10 (11):
  • [6] Galvanic Corrosion Behavior of the X80 Steel Welded Joint
    Li, Yadong
    Sang, Jiaxu
    Yang, Yunzhi
    Fang, Guoxin
    Pang, Jianjun
    Liu, Feng
    COATINGS, 2024, 14 (05)
  • [7] Passivity and Pitting Corrosion of X80 Pipeline Steel in Carbonate/Bicarbonate Solution Studied by Electrochemical Measurements
    Xue, H. B.
    Cheng, Y. F.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2010, 19 (09) : 1311 - 1317
  • [8] Influence of Crevice Thickness on Corrosion Behavior of API X80 Steel under Disbonded Coating in Acid Soil Environment
    Zhao, Bo
    Wan, Hongxia
    Peng, Yunyan
    Liu, Chao
    Li, Jun
    Shou, Binan
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (01): : 1 - 11
  • [9] The Influence of O2 on the Corrosion Behavior of the X80 Steel in CO2 Environment
    Wang, Xiao
    Wang, Xinyue
    Wang, Jun
    Wang, Guowei
    Pan, Yi
    Yan, Shuangchun
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01): : 889 - 898
  • [10] CORROSION BEHAVIOR OF X80 STEEL IN YINGTAN SOIL SIMULATED SOLUTION UNDER DISBONDED COATING
    Zhao Bo
    Du Cuiwei
    Liu Zhiyong
    Li Xiaogang
    Yang Jike
    Li Yueqiang
    ACTA METALLURGICA SINICA, 2012, 48 (12) : 1530 - 1536
12345