Intuitive Analysis of the Microtribological Behavior of Copper-Coated Graphite-Graphite/Cu Composites with High Graphite Contents

被引:10
|
作者
Zhu, Linying [1 ]
Yi, Maozhong [1 ]
Ge, Yicheng [1 ]
Zhang, Bei [1 ]
Xie, Aolin [1 ]
机构
[1] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Peoples R China
来源
ACS OMEGA | 2022年 / 7卷 / 32期
关键词
TRIBOLOGICAL PROPERTIES; THERMAL-CONDUCTIVITY; MICROSTRUCTURE; WEAR; FRICTION; TEMPERATURE;
D O I
10.1021/acsomega.2c01276
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
To improve the combination of graphite and copper, the friction and wear of a graphite/copper composite with a high content of graphite (50 wt %), copper-coated graphite were used to modify it. To observe the distribution law of each phase in the material and the change of composite surface structure after the friction and wear experiment, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the micro-structure, friction film, debris, and friction cross section of the composites. The results show that the large particle size of copper-coated graphite is anisotropic in the material, which helps to form a friction film with a high graphite content on the contact surface. TEM images of the friction film and debris directly reflect the structure changes of graphite and copper during friction; under normal load and shear force, interlamellar detachment and interlamellar fracture of graphite occur, and its edge is folded and crimped, resulting in the loss of an ordered state in some regions, which results in the instability of crystal lattice and the transition from an ordered to disordered state of graphite, resulting in the (002) halo ring in FFT results. Severe plastic deformation and oxidation reactions occur in copper, and copper oxides are formed, forming a high-strength and smooth oxide film in the metal-rich area and improving the wear resistance of the material. TEM images of the friction section directly show that an inverted triangular deformation zone is formed on the surface of the sample after friction and wear experiments. The edge of the deformation zone is stepped, consisting of a drag zone and an accumulation zone, and the surface of the contact zone is covered by a carbon film.
引用
收藏
页码:28217 / 28225
页数:9
相关论文
共 50 条
  • [31] Nano-scale copper-coated graphite as anode material for lithium-ion batteries
    Guo, K
    Pan, Q
    Wang, L
    Fang, S
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2002, 32 (06) : 679 - 685
  • [32] FRACTURE-BEHAVIOR OF COATED UNCOATED GRAPHITE-EPOXY COMPOSITES
    JOSEPH, R
    BELL, JP
    RHEE, H
    POLYMER ENGINEERING AND SCIENCE, 1988, 28 (09): : 605 - 609
  • [33] Effect of high graphite filler contents on the mechanical and tribological failure behavior of epoxy matrix composites
    Baptista, R.
    Mendao, A.
    Rodrigues, F.
    Figueiredo-Pina, C. G.
    Guedes, M.
    Marat-Mendes, R.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2016, 85 : 113 - 124
  • [34] On the tribological behaviors of Cu matrix composites with different Cu-coated graphite content
    Li, Hengqing
    Liu, Yangzhen
    Zheng, Baochao
    Wang, Shuai
    Yi, Yanliang
    Zhang, Yongzhen
    Li, Wei
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 25 : 83 - 94
  • [35] Interface and properties of copper matrix composites reinforced with TiC coated spherical graphite
    Wang, Xulei
    He, Xinbo
    Zhang, Ren
    Guan, Dandan
    Liu, Rongjun
    Qu, Xuanhui
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [36] Effect of sintering parameters on friction wear behavior of graphite/copper composites
    Jin Yong-ping
    Xiang Chun
    Cui Liang-ping
    Guo Bin
    VACUUM TECHNOLOGY AND SURFACE ENGINEERING - PROCEEDINGS OF THE 9TH VACUUM METALLURGY AND SURFACE ENGINEERING CONFERENCE, 2009, : 215 - +
  • [37] Decomposition behavior and thermoelectric properties of copper selenide-graphite composites
    Staab, Lennart
    Koetzsch, Torsten
    Noack, Tom Jonathan
    Oeckler, Oliver
    APPLIED PHYSICS LETTERS, 2023, 122 (08)
  • [38] Wetting Behavior of Graphite and CFC Composites by Cu-Ti Compacts
    Wang Ke
    Mao Yangwu
    Deng Quanrong
    Nie Dunwei
    Mombello, Domenico
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2018, 33 (01): : 35 - 42
  • [39] Wetting Behavior of Graphite and CFC Composites by Cu-Ti Compacts
    王珂
    毛样武
    DENG Quanrong
    NIE Dunwei
    MOMBELLO Domenico
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2018, 33 (01) : 35 - 42
  • [40] Wetting behavior of graphite and CFC composites by Cu-Ti compacts
    Ke Wang
    Yangwu Mao
    Quanrong Deng
    Dunwei Nie
    Domenico Mombello
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2018, 33 : 35 - 42