Intuitive Analysis of the Microtribological Behavior of Copper-Coated Graphite-Graphite/Cu Composites with High Graphite Contents

被引:10
|
作者
Zhu, Linying [1 ]
Yi, Maozhong [1 ]
Ge, Yicheng [1 ]
Zhang, Bei [1 ]
Xie, Aolin [1 ]
机构
[1] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Peoples R China
来源
ACS OMEGA | 2022年 / 7卷 / 32期
关键词
TRIBOLOGICAL PROPERTIES; THERMAL-CONDUCTIVITY; MICROSTRUCTURE; WEAR; FRICTION; TEMPERATURE;
D O I
10.1021/acsomega.2c01276
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
To improve the combination of graphite and copper, the friction and wear of a graphite/copper composite with a high content of graphite (50 wt %), copper-coated graphite were used to modify it. To observe the distribution law of each phase in the material and the change of composite surface structure after the friction and wear experiment, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the micro-structure, friction film, debris, and friction cross section of the composites. The results show that the large particle size of copper-coated graphite is anisotropic in the material, which helps to form a friction film with a high graphite content on the contact surface. TEM images of the friction film and debris directly reflect the structure changes of graphite and copper during friction; under normal load and shear force, interlamellar detachment and interlamellar fracture of graphite occur, and its edge is folded and crimped, resulting in the loss of an ordered state in some regions, which results in the instability of crystal lattice and the transition from an ordered to disordered state of graphite, resulting in the (002) halo ring in FFT results. Severe plastic deformation and oxidation reactions occur in copper, and copper oxides are formed, forming a high-strength and smooth oxide film in the metal-rich area and improving the wear resistance of the material. TEM images of the friction section directly show that an inverted triangular deformation zone is formed on the surface of the sample after friction and wear experiments. The edge of the deformation zone is stepped, consisting of a drag zone and an accumulation zone, and the surface of the contact zone is covered by a carbon film.
引用
收藏
页码:28217 / 28225
页数:9
相关论文
共 50 条
  • [21] Enhanced mechanical and tribological properties of copper matrix composites reinforced by copper-coated graphite and Ti3AlC2
    Liu, Xiao
    Cao, Xinjian
    Yi, Xiaoyang
    Wang, Haizhen
    Guo, Jie
    Yang, Jun
    MATERIALS TODAY COMMUNICATIONS, 2024, 38
  • [22] Tribological Behavior of Copper-Graphite Composites Reinforced with Cu-Coated or Uncoated SiO2 Particles
    Zou, Haohao
    Ran, Xu
    Zhu, Weiwei
    Wang, Yong
    Zhan, Siqi
    Hao, Zhikang
    MATERIALS, 2018, 11 (12)
  • [23] Thermal expansion of Cu/graphite composites: effect of copper coating
    Kovacik, J.
    Emmer, S.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2011, 49 (06): : 411 - 416
  • [24] Role of Cr-carbide Coating on Graphite Particles in the Mechanical and Wear Behavior of Graphite/Copper Composites
    Hou, Baoqiang
    Zhang, Nanlong
    Zhi, Qiang
    Zhou, Xiaonan
    Wang, Bo
    Yang, Jianfeng
    TRIBOLOGY LETTERS, 2024, 72 (01)
  • [25] Role of Cr-carbide Coating on Graphite Particles in the Mechanical and Wear Behavior of Graphite/Copper Composites
    Baoqiang Hou
    Nanlong Zhang
    Qiang Zhi
    Xiaonan Zhou
    Bo Wang
    Jianfeng Yang
    Tribology Letters, 2024, 72
  • [26] Microstructures and Properties of Resin Carbon-Coated Graphite/Copper Composites
    Xiao Peng
    Jiang Xu
    Zhu Jiamin
    Liu Tan
    Fang Huachan
    RARE METAL MATERIALS AND ENGINEERING, 2019, 48 (10) : 3265 - 3274
  • [27] Microstructures and Properties of Resin Carbon-Coated Graphite/Copper Composites
    Xiao, Peng
    Jiang, Xu
    Zhu, Jiamin
    Liu, Tan
    Fang, Huachan
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2019, 48 (10): : 3265 - 3274
  • [28] Study on tribological behaviors of copper coated graphite filled PTFE composites
    Yan, Fengyuan
    Li, Fei
    Liu, Weimin
    Liu, Chengyu
    Mocaxue Xuebao/Tribology, 1999, 19 (01): : 7 - 11
  • [29] EFFECT OF HEATING ON THE BEHAVIOR OF COPPER-GRAPHITE COMPOSITES WITH A BINDER
    KUZMINA, IV
    RODIONOV, NV
    RASSKAZOVA, EG
    POWDER METALLURGY AND METAL CERAMICS, 1994, 33 (3-4) : 165 - 167
  • [30] Nano-scale copper-coated graphite as anode material for lithium-ion batteries
    K. Guo
    Q. Pan
    L. Wang
    S. Fang
    Journal of Applied Electrochemistry, 2002, 32 : 679 - 685