Non-equiatomic FeNiCoAl-based high entropy alloys with multiscale heterogeneous lamella structure for strength and ductility

被引:61
作者
Zhang, Cheng [1 ]
Zhu, Chaoyi [1 ]
Vecchio, Kenneth [1 ,2 ]
机构
[1] Univ Calif San Diego, Mat Sci & Engn Program, La Jolla, CA 92093 USA
[2] Univ Calif San Diego, Dept NanoEngn, 9500 Gilman Dr,MC-0448, La Jolla, CA 92093 USA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2019年 / 743卷
关键词
Non-equiatomic; High entropy alloy; Heterogeneous lamella structure; Geometrically necessary dislocations; Back stress; PARTIAL RECRYSTALLIZATION; MECHANICAL-PROPERTIES; SHEAR LOCALIZATION; STAINLESS-STEEL; PHASE-STABILITY; BACK STRESS; MICROSTRUCTURE; DEFORMATION; DESIGN; ENHANCEMENT;
D O I
10.1016/j.msea.2018.11.073
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A new method based on conventional thermomechanical processing is proposed for design of non-equiatomic FeNiCoAlTaB (NCATB) high entropy alloy (HEA) with multiscale heterogeneous lamella (HL) structures to achieve outstanding mechanical properties. Two kinds of microstructures are produced in this study: 1) specimens annealed at 1050 degrees C exhibit structure composed of fine grains and ultrafine grains, which exhibits a combination of high strength (UTS similar to 1050 MPa) and good ductility (elongation similar to 23%); and 2) specimens annealed at 1200 degrees C which exhibit structure composed of fine grains and coarse grains, which demonstrates excellent synergy of good strength (UTS similar to 890 MPa) and exceptional ductility (elongation similar to 43%). It has been shown that shear bands formed in the cold rolling step are responsible for the fine-grain area in both specimens. Additionally, precipitation of NiAl (B2) particles also affects the formation of HL structures due to Zener pinning effect. The back-stress strengthening mechanism, responsible for high strength and ductility, is verified through combined "loading-unloading-reloading" (LUR) cyclic tensile tests and electron backscatter diffraction (EBSD) based geometrically necessary dislocation (GND) density analysis.
引用
收藏
页码:361 / 371
页数:11
相关论文
共 64 条
  • [1] DEFORMATION OF PLASTICALLY NON-HOMOGENEOUS MATERIALS
    ASHBY, MF
    [J]. PHILOSOPHICAL MAGAZINE, 1970, 21 (170): : 399 - &
  • [2] Trade-off between tensile property and formability by partial recrystallization of CrMnFeCoNi high-entropy alloy
    Bae, Jae Wung
    Moon, Jongun
    Jang, Min Ji
    Yim, Dami
    Kim, Daeyong
    Lee, Sunghak
    Kim, Hyoung Seop
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 703 : 324 - 330
  • [3] STRUCTURE OF DEFORMED ALUMINUM AND ITS RECRYSTALLIZATION - INVESTIGATIONS WITH TRANSMISSION KOSSEL DIFFRACTION
    BELLIER, SP
    DOHERTY, RD
    [J]. ACTA METALLURGICA, 1977, 25 (05): : 521 - 538
  • [4] Texture enhancement during grain growth of magnesium alloy AZ31B
    Bhattacharyya, J. J.
    Agnew, S. R.
    Muralidharan, G.
    [J]. ACTA MATERIALIA, 2015, 86 : 80 - 94
  • [5] Microstructural development in equiatomic multicomponent alloys
    Cantor, B
    Chang, ITH
    Knight, P
    Vincent, AJB
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 375 : 213 - 218
  • [6] Microstructure-grain orientation relationship in coarse grain nickel cold-rolled to large strain
    Chen, H. S.
    Godfrey, A.
    Hansen, N.
    Xie, J. X.
    Liu, Q.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 483-84 : 157 - 160
  • [7] A COMPARISON OF 2 SIMPLE METHODS FOR MEASURING CYCLIC INTERNAL AND EFFECTIVE STRESSES
    DICKSON, JI
    BOUTIN, J
    HANDFIELD, L
    [J]. MATERIALS SCIENCE AND ENGINEERING, 1984, 64 (01): : L7 - L11
  • [8] ESHELBY JD, 1951, PHILOS MAG, V42, P351
  • [9] Revealing Extraordinary Intrinsic Tensile Plasticity in Gradient Nano-Grained Copper
    Fang, T. H.
    Li, W. L.
    Tao, N. R.
    Lu, K.
    [J]. SCIENCE, 2011, 331 (6024) : 1587 - 1590
  • [10] On the origin of the tensile flow stress in the stainless steel AISI 316L at 300 K: Back stress and effective stress
    Feaugas, X
    [J]. ACTA MATERIALIA, 1999, 47 (13) : 3617 - 3632