Microstructural morphology of rheocast A319 aluminium alloy

被引:6
作者
Aziz, Ahmad Muhammad [1 ]
Omar, Mohd Zaidi [1 ,2 ]
Sajuri, Zainuddin [1 ,2 ]
Salleh, Mohd Shukor [3 ]
机构
[1] Univ Kebangsaan Malaysia, Fac Engn & Built Environm, Dept Mech & Mat Engn, Bangi 43600, Selangor, Malaysia
[2] Univ Kebangsaan Malaysia, Fac Engn & Built Environm, Ctr Automot Res, Bangi, Malaysia
[3] Univ Tekn Malaysia Melaka, Fac Mfg Engn, Dept Mfg Proc, Durian Tunggal, Malaysia
关键词
Semi-solid processing; cooling slope; nucleation; evolution; intermetallic compound; AL-SI ALLOYS; COOLING SLOPE; MECHANICAL-PROPERTIES; SEMISOLID MICROSTRUCTURE; INTERMETALLIC COMPOUNDS; THERMAL-ANALYSIS; EVOLUTION; CAST; SILICON; CU;
D O I
10.1177/1687814016649354
中图分类号
O414.1 [热力学];
学科分类号
摘要
This article examines the evolution of the microstructure of A319 aluminium alloy as it flows along a cooling slope plate and discusses the type and influence of the intermetallic compounds thus formed. Numerous past research studies have analysed the microstructural transformation of alloys in a mould, but few researchers have investigated this phenomenon on the cooling slope plate. A change in the microstructure of the alloy from dendritic to non-dendritic is clearly obtained as the alloy moves from the impact zone to bottom zone on the cooling slope plate. It is important to clarify the mechanism of microstructural evolution through nucleation and fragmentation of the primary phase arm for fundamental understanding of research. Analysis by optical microscope and scanning electron microscope reveals the evolution of the microstructure and intermetallic compounds of A319 as it progresses along the cooling slope plate. The Vickers test was used to determine the hardness of the alloy thus produced. The results show the influence of the mould in obtaining a spheroidal microstructure; the microstructure in the bottom zone of the cooling slope plate is nearly spheroidal rather than fully spheroidal. The hardness of the alloy is enhanced when the microstructure is spheroidal and when the Mg2Si compound is present in the alloy.
引用
收藏
页码:1 / 10
页数:10
相关论文
共 53 条
[11]   Developments in the processing and properties of particulate Al-Si composites [J].
Ejiofor, JU ;
Reddy, RG .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1997, 49 (11) :31-37
[12]  
Elia FD, 2009, THESIS RYERSON U TOR
[13]  
Gruzleski J.E., 1990, The Treatment of Aluminum-Silicon Alloys, P256
[14]  
Gruzleski JE, 2000, MICROSTRUCTURE DEV M, P244
[15]  
GUO H M, 2006, ACTA METALLURGICA SI, V19, P328, DOI DOI 10.1016/S1006-7191(06)62069-3
[16]   Simple rheocasting processes [J].
Haga, T ;
Kapranos, P .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2002, 130 :594-598
[17]   Billetless simple thixoforming process [J].
Haga, T ;
Kapranos, P .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2002, 130 :581-586
[18]   Casting of aluminum alloy ingots for thixoforming using a cooling slope [J].
Haga, T ;
Suzuki, S .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2001, 118 (1-3) :169-172
[19]   Modification of eutectic silicon in Al-Si alloys [J].
Hegde, Sathyapal ;
Prabhu, K. Narayan .
JOURNAL OF MATERIALS SCIENCE, 2008, 43 (09) :3009-3027
[20]  
Hrivnak N, 1996, ASM SPECIALTY HDB AL, P784