NiAl Matrix High-Temperature Self-Lubricating Composite

被引：31
作者：
Zhu, Shengyu [1 ,2 ]
Bi, Qinling [1 ]
Wu, Hairong [1 ,2 ]
Yang, Jun [1 ]
Liu, Weimin [1 ]
机构：
[1] Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China
[2] Chinese Acad Sci, Grad Univ, Beijing 100039, Peoples R China
来源：
TRIBOLOGY LETTERS | 2011年 / 41卷 / 03期
基金：
中国国家自然科学基金;
关键词：
NiAl matrix; High temperature; Self-lubricating composite; Wear; TRIBOLOGICAL PROPERTIES; SLIDING WEAR; MECHANICAL-PROPERTIES; METALS; PM212; CR;
D O I：
10.1007/s11249-010-9727-9
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A high-temperature self-lubricating composite NiAl-Cr-Mo-CaF2 was fabricated using the powder metallurgy technique, and the tribological behavior of the composite at a wide range of temperatures (room temperature to 1000 A degrees C) was investigated. The results showed that the composite had a favorable friction coefficient of about 0.2 and an excellent wear resistance of about 1 x 10(-5) mm(3)N(-1)m(-1) at the high temperatures tested (800 and 1000 A degrees C). The excellent self-lubricating performance was attributed to the formation of the glaze film on the worn surface consisting mainly of CaCrO4 and CaMoO4 as high-temperature solid lubricants.
引用
收藏
页码：535 / 540
页数：6
相关论文
共 50 条
[1]   NiAl Matrix High-Temperature Self-Lubricating Composite [J].
Shengyu Zhu ;
Qinling Bi ;
Hairong Wu ;
Jun Yang ;
Weimin Liu .
Tribology Letters, 2011, 41 :535-540
[2]   NiAl Matrix Self-Lubricating Composite at a Wide Temperature Range [J].
Zhu, Shengyu ;
Kong, Lingqian ;
Li, Fei ;
Yang, Jun ;
Ma, Jiqiang ;
Cheng, Jun ;
Zhen, Jinming ;
Qiao, Zhuhui .
JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2015, 137 (02)
[3]   High-temperature wear behavior of self-lubricating Co matrix alloys prepared by P/M [J].
Cui, Gongjun ;
Han, Junrui ;
Wu, Guoxiong .
WEAR, 2016, 346 :116-123
[4]   Ni3Al matrix high temperature self-lubricating composites [J].
Zhu, Shengyu ;
Bi, Qinling ;
Yang, Jun ;
Liu, Weimin ;
Xue, Qunji .
TRIBOLOGY INTERNATIONAL, 2011, 44 (04) :445-453
[5]   A novel CoCrFeNi high entropy alloy matrix self-lubricating composite [J].
Zhang, Aijun ;
Han, Jiesheng ;
Su, Bo ;
Meng, Junhu .
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 725 :700-710
[6]   Microstructure and High-Temperature Wear Performance of FeCr Matrix Self-Lubricating Composites from Room Temperature to 800 °C [J].
Cui, Gongjun ;
Liu, Yanping ;
Gao, Guijun ;
Liu, Huiqiang ;
Kou, Ziming .
MATERIALS, 2020, 13 (01)
[7]   High-temperature tribological properties of the novel NiCr(MoNb)x-Ag self-lubricating composite films [J].
Zhang, Hong ;
Zhang, Rui ;
Zhao, Xiaoyu ;
Li, Xindong ;
Chen, Botong ;
Li, Yuhong ;
Wang, Peng .
SURFACE & COATINGS TECHNOLOGY, 2023, 471
[8]   Microstructure, mechanical properties and tribological performance of CoCrFeNi high entropy alloy matrix self-lubricating composite [J].
Zhang, Aijun ;
Han, Jiesheng ;
Su, Bo ;
Li, Pengde ;
Meng, Junhu .
MATERIALS & DESIGN, 2017, 114 :253-263
[9]   High Temperature Lubricating Behavior of NiAl Matrix Composites With Addition of CuO [J].
Zhu, Shengyu ;
Cheng, Jun ;
Qiao, Zhuhui ;
Tian, Yuan ;
Yang, Jun .
JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2016, 138 (03)
[10]   Tribological Performance of NiAl Self-lubricating Matrix Composite with Addition of Graphene at Different Loads [J].
Xiao, Yecheng ;
Shi, Xiaoliang ;
Zhai, Wenzheng ;
Yao, Jie ;
Xu, Zengshi ;
Chen, Long ;
Zhu, Qingshuai .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (08) :2866-2874
12345