Light emitting diode structure based on Si nanocrystals formed by implantation into thermal oxide

被引：103

作者：

Lalic, N ^{[1
]}

Linnros, J ^{[1
]}

机构：

[1] Royal Inst Technol, Dept Elect, S-16440 Kista, Sweden

来源：

JOURNAL OF LUMINESCENCE | 1998年 / 80卷 / 1-4期

关键词：

silicon nanocrystal; electroluminescence; LED; ion implantation;

D O I：

10.1016/S0022-2313(98)00109-4

中图分类号：

O43 [光学];

学科分类号：

070207 ; 0803 ;

摘要：

Light emitting diodes (LED), continuously operable at room temperature, have been fabricated by Si (+) ion implantation into SiO2 and subsequent annealing in order to form Si nanocrystals. A highly doped poly-Si layer was used to enhance injection into nanocrystals. Visible electroluminescence (EL) was observed from the LEDs with oxide thickness less than or equal to 180 Angstrom for bias voltages above 8 V. The EL decay transient was similar to stretched-exponential decays observed for photoluminescence (PL) from Si nanocrystals. (C) 1999 Elsevier Science B.V. All rights reserved.

引用

页码：263 / 267

页数：5

共 16 条

[1] ATWATER HA, 1994, MATER RES SOC SYMP P, V316, P409
[2] Tuning the emission wavelength of Si nanocrystals in SiO2 by oxidation
Brongersma, ML
Polman, A
Min, KS
Boer, E
Tambo, T
Atwater, HA
[J]. APPLIED PHYSICS LETTERS, 1998, 72 (20) : 2577 - 2579
[3] DARGYS A, 1994, HDB PHYSICAL PROPERT, P102
[4] Continuously tunable photoluminescence from Si+-implanted and thermally annealed SiO2 films
Fischer, T
PetrovaKoch, V
Shcheglov, K
Brandt, MS
Koch, F
[J]. THIN SOLID FILMS, 1996, 276 (1-2) : 100 - 103
[5] Visible light emission from Si nanocrystals grown by ion implantation and subsequent annealing
Guha, S
Pace, MD
Dunn, DN
Singer, IL
[J]. APPLIED PHYSICS LETTERS, 1997, 70 (10) : 1207 - 1209
[6] -Iwayama T. S., 1993, J PHYS CONDENS MATT, V5, pL375, DOI DOI 10.1088/0953-8984/5/31/002
[7] Photoluminescence mechanism in surface-oxidized silicon nanocrystals
Kanemitsu, Y
Okamoto, S
Otobe, M
Oda, S
[J]. PHYSICAL REVIEW B, 1997, 55 (12) : R7375 - R7378
[8] Characterization of a porous silicon diode with efficient and tunable electroluminescence
Lalic, N
Linnros, J
[J]. JOURNAL OF APPLIED PHYSICS, 1996, 80 (10) : 5971 - 5977
[9] HIGH QUANTUM EFFICIENCY FOR A POROUS SILICON LIGHT-EMITTING DIODE UNDER PULSED OPERATION
LINNROS, J
LALIC, N
[J]. APPLIED PHYSICS LETTERS, 1995, 66 (22) : 3048 - 3050
[10] LINNROS J, UNPUB

← 1 2 →