Influence of residual stresses from shot peening on fretting fatigue crack growth

被引:11
作者
Cadario, A. [1 ]
Alfredsson, B. [1 ]
机构
[1] Royal Inst Technol, Dept Solid Mech, SE-10044 Stockholm, Sweden
关键词
fatigue crack growth; finite element method; fretting fatigue; peening; residual stress relaxation;
D O I
10.1111/j.1460-2695.2007.01165.x
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
One method to improve fretting fatigue life is to shot peen the contact surfaces. Experimental fretting life results from specimens in a Titanium alloy with and without shot peened surfaces were evaluated numerically. The residual stresses were measured at different depths below the fretting scar and compared to the corresponding residual stress profile of an unfretted surface. Thus, the amount of stress relaxation during fretting tests was estimated. Elastic-plastic finite element computations showed that stress relaxation was locally more significant than that captured in the measurements. Three different numerical fatigue crack growth models were compared. The best agreement between experimental and numerical fatigue lives for both peened and unpeened specimens was achieved with a parametric fatigue growth procedure that took into consideration the growth behaviour along the whole front of a semi-elliptical surface crack. Furthermore, the improved fretting fatigue life from shot peening was explained by slower crack growth rates in the shallow surface layer with compressive residual stresses from shot peening. The successful life analyses hinged on three important issues: an accurate residual stress profile, a sufficiently small start crack and a valid crack growth model.
引用
收藏
页码:947 / 963
页数:17
相关论文
共 29 条
[21]  
*NASGRO, 2002, NASGRO 4 22
[22]   A CONSISTENT FEW PARAMETER CRACK-GROWTH DESCRIPTION PROCEDURE [J].
NILSSON, F .
INTERNATIONAL JOURNAL OF FRACTURE, 1992, 54 (01) :35-44
[23]  
NILSSON L, 1988, 9811 SAQ FOU
[24]   Recent developments in the understanding of fretting fatigue [J].
Nowell, D ;
Dini, D ;
Hills, DA .
ENGINEERING FRACTURE MECHANICS, 2006, 73 (02) :207-222
[25]  
Pommier S, 2000, FATIGUE FRACT ENG M, V23, P129, DOI 10.1046/j.1460-2695.2000.00259.x
[26]   Measurement of fatigue crack closure for negative stress ratio [J].
Romeiro, FFJ ;
Domingos, CA ;
de Freitas, MJM .
ADVANCES IN FATIGUE CRACK CLOSURE MEASUREMENT AND ANALYSIS: VOL 2, 1999, 1343 :321-336
[27]   A closure, model to crack growth under large-scale yielding and through residual, stress fields [J].
Wang, CH ;
Barter, SA ;
Liu, Q .
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2003, 125 (02) :183-190
[28]   RESIDUAL-STRESS AND SURFACE-ROUGHNESS IN FRETTING FATIGUE [J].
WATERHOUSE, RB ;
TROWSDALE, AJ .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1992, 25 (1A) :A236-A239
[29]  
Wu Xue-Ren., 1991, WEIGHT FUNCTIONS STR