Assessing the degradation performance of ultrahigh-purity magnesium in vitro and in vivo

被引：103

作者：

Hofstetter, Joelle ^{[1
]}

Martinelli, Elisabeth ^{[2
]}

Weinberg, Annelie M. ^{[2
]}

Becker, Minh ^{[1
]}

Mingler, Bernhard ^{[3
]}

Uggowitzer, Peter J. ^{[1
]}

Loeffler, Jorg F. ^{[1
]}

机构：

[1] ETH, Dept Mat, Lab Met Phys & Technol, CH-8093 Zurich, Switzerland

[2] Med Univ Graz, Dept Orthopaed & Orthopaed Surg, A-8036 Graz, Austria

[3] AIT Austrian Inst Technol GmbH, Hlth & Environm Dept, A-2700 Wr Neustadt, Austria

来源：

CORROSION SCIENCE | 2015年 / 91卷

关键词：

Magnesium; SEM; SIMULATED BODY-FLUID; PURE MAGNESIUM; BIODEGRADATION PERFORMANCE; CORROSION; ALLOYS; MG; IMPLANTS; HYDROGEN;

D O I：

10.1016/j.corsci.2014.09.008

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The biodegradation of ultrahigh-purity Mg (XHP Mg, Fe approximate to 2 ppm) was tested in vitro in NaHCO3/CO2-buffered simulated body fluid and in vivo in the femur of rats. The in vitro degradation rate, which was evaluated using an also here described newly designed hydrogen evolution testing setup, is with approximate to 10 +/- 3 mu m/y very low and shows very good agreement with in vivo data. The results for XHP Mg are also compared with in vitro tests on high-purity Mg (Few approximate to 37 ppm) in the as-cast and annealed states. The less pure specimens exhibit significantly higher degradation rates due to the formation of Fe-containing precipitates during casting and annealing. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：29 / 36

页数：8

共 39 条

[1] Corrosion of high purity Mg, Mg2Zn0.2Mn, ZE41 and AZ91 in Hank's solution at 37 °C [J].

Abidin, Nor Ishida Zainal ;

Atrens, Aleks D. ;

Martin, Darren ;

Atrens, Andrej .

CORROSION SCIENCE, 2011, 53 (11) :3542-3556

[2]

Adamson K, 1994, CORROSION, P4

[3]

[Anonymous], 2012, [No title captured], Patent No. 2013107644

[4]

*ASTM INT, 2004, STAND PRACT LAB IMM

[5] Corrosion mechanism applicable to biodegradable magnesium implants [J].

Atrens, Andrej ;

Liu, Ming ;

Abidin, Nor Ishida Zainal .

MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2011, 176 (20) :1609-1636

[6] SOLUBILITY OF HYDROGEN IN WATER IN A BROAD TEMPERATURE AND PRESSURE RANGE [J].

BARANENKO, VI ;

KIROV, VS .

SOVIET ATOMIC ENERGY, 1989, 66 (01) :30-34

[7]

BARTON RS, 1960, ATOMIC ENERGY RES ES

[8]

Campbell J., 2003, CASTINGS, V2nd

[9] Corrosion of ultra-high-purity Mg in 3.5% NaCl solution saturated with Mg(OH)2 [J].

Cao, Fuyong ;

Shi, Zhiming ;

Hofstetter, Joelle ;

Uggowitzer, Peter J. ;

Song, Guangling ;

Liu, Ming ;

Atrens, Andrej .

CORROSION SCIENCE, 2013, 75 :78-99

[10] On the in vitro and in vivo degradation performance and biological response of new biodegradable Mg-Y-Zn alloys [J].

Haenzi, Anja C. ;

Gerber, Isabel ;

Schinhammer, Michael ;

Loeffler, Joerg F. ;

Uggowitzer, Peter J. .

ACTA BIOMATERIALIA, 2010, 6 (05) :1824-1833

← 1 2 3 4 →