Phase characterization of debris generated in brake pad coefficient of friction tests

Debris from coefficient of friction (COF) tests with semimetallic vehicle brake pads tested against cast iron discs in a full scale inertial bench dynamometer were characterized with Mossbauer spectroscopy, X-ray diffraction and scanning electron microscopy. The debris was collected during 4 brake test runs that consisted of short and long burnishing procedures (100 and 200 cycles) followed by 1000 full stops decelerating from low and high speed (from 46 and 96 km/h). At the low speed tests the COF was high and stable and the debris had increased magnetite content. At the high speed stops COF was lower and more erratic and the debris showed high cementite content. Cementite formation should be prevented in order to get stable COF. (C) 2011 Elsevier B.V. All rights reserved.