Effect of temperature on the fracture behavior of polyamide 12 and glass-filled polyamide 12 processed by selective laser sintering

被引：57

作者：

Cano, A. J. ^{[1
]}

Salazar, A. ^{[1
]}

Rodriguez, J. ^{[1
]}

机构：

[1] Univ Rey Juan Carlos, DIMME, Grp Durabilidad & Integridad Mecan Mat Estruct, C Tulipan S-N, Madrid 28933, Spain

来源：

ENGINEERING FRACTURE MECHANICS | 2018年 / 203卷

关键词：

Selective laser sintering; Polyamide; 12; Fracture toughness; MECHANICAL-PROPERTIES; COMPOSITES; NYLON-12; PARTS;

D O I：

10.1016/j.engfracmech.2018.07.035

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

The influence of the orientation and of the temperature on the mechanical properties of the polyamide 12 (PA12) and the polyamide 12 reinforced with glass beads processed via Selective Laser Sintering was analyzed. Tensile and fracture tests were performed at -50 degrees C, 23 degrees C and 50 degrees C with applied load perpendicular and parallel to the layered structure. The fracture resistance of PA12 was higher than that of the composite due to the poor adhesion of the glass beads to the matrix. The fracture behavior of the composite was unaffected by the temperature and the orientation. J(IC) values of PA12 were similar at -50 degrees C and at 23 degrees C and much lower than at 50 degrees C. The anisotropy was relevant during the stable crack growth.

引用

页码：66 / 80

页数：15

共 31 条

[1]

[Anonymous], F279212A ASTM

[2]

[Anonymous], 2000, PLAST DET FRACT TOUG

[3]

[Anonymous], 2016, WHOLERS REPORT 3D PR

[4]

[Anonymous], 2007, E182006 ASTM

[5] Materials for additive manufacturing [J].

Bourell, David ;

Kruth, Jean Pierre ;

Leu, Ming ;

Levy, Gideon ;

Rosen, David ;

Beese, Allison M. ;

Clare, Adam .

CIRP ANNALS-MANUFACTURING TECHNOLOGY, 2017, 66 (02) :659-681

[6] Performance limitations in polymer laser sintering [J].

Bourell, David L. ;

Watt, Trevor J. ;

Leigh, David K. ;

Fulcher, Ben .

8TH INTERNATIONAL CONFERENCE ON LASER ASSISTED NET SHAPE ENGINEERING (LANE 2014), 2014, 56 :147-156

[7] Fracture mechanics of laser sintered cracked polyamide for a new method to induce cracks by additive manufacturing [J].

Brugo, T. ;

Palazzetti, R. ;

Ciric-Kostic, S. ;

Yan, X. T. ;

Minak, G. ;

Zucchelli, A. .

POLYMER TESTING, 2016, 50 :301-308

[8]

Castillo Acero M.A., 2017, P 8 ECCOMAS THEM C S

[9] Dependence of mechanical properties of polyamide components on build parameters in the SLS process [J].

Caulfield, B. ;

McHugh, P. E. ;

Lohfeld, S. .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 182 (1-3) :477-488

[10] Development of a characterization approach for the sintering behavior of new thermoplastics for selective laser sintering [J].

Drummer, Dietmar ;

Rietzel, Dominik ;

Kuehnlein, Florian .

LASER ASSISTED NET SHAPE ENGINEERING 6, PROCEEDINGS OF THE LANE 2010, PART 2, 2010, 5 :533-542

← 1 2 3 4 →