Mechanical strength and microstructural observations for remaining life assessment of service exposed 24Ni-24Cr-1.5Nb cast austenitic steel reformer tubes

被引:16
作者
Swaminathan, Jaganathan [1 ]
Prasad, Prabha [1 ]
Gunian, Manoj Kumar [1 ]
Gugloth, Krishna [1 ]
Roy, Prabir Kumar [1 ]
Singh, Raghubir [1 ]
Ghosh, Rabindranath [1 ]
机构
[1] Natl Met Lab, Div Mat Sci & Technol, Jamshedpur 831007, Jharkhand, India
关键词
remaining life assessment; heater tubes; creep; austenitic alloys;
D O I
10.1016/j.engfailanal.2007.06.009
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Reformer furnace heater tubes made of cast austenitic alloy steels serve in the temperature range of 1073-1173 K and pressure around 3-4 MPa. Though the design life is about 100,000 h (similar to 11.4 years), premature failures within 3-8 years are more common, mainly caused by premature creep induced by overheating. The cast tube material undergoes microstructural changes with service exposure and as a consequence, degradation in strength. Microstructural changes, tensile strength and accelerated stress rupture strength of 96,000, 105,120 and 131,400 h service exposed tubes of 24%Ni24%Cr1.5%Nb alloy (equivalent to IN-519) served in a reformer furnace were analysed. Presence of coarsened carbides at the interdendritic boundaries, absence of significant amount of secondary carbides in the intra-dendritic regions together with sigma (a) phase at both inter and intra-dendritic regions and isolated creep cavities indicated severity of service induced ageing and damage process accumulation. However, the stress rupture life obtained through Larson-Miller parametric method was good for further life extension. Attempts to correlate the microstructurall changes to remaining creep life assessment (RLA) proved to be difficult as errors were mainly arising from the fact that temperature experienced by the individual tubes in a furnace differs and for a single tube through out its vertical length it varies. Non-destructive ultrasonic scan method employed too could not estimate the creep damage level accurately and the results vary with destructive test results. Lack of data on both microstructural changes and mechanical strength of the service exposed tube materials makes RLA more difficult. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码:723 / 735
页数:13
相关论文
共 17 条
[1]   Microstructural factors that determine the weldability of a high Cr-high SiHK 40 alloy [J].
Haro, S ;
López, D ;
Velasco, A ;
Viramontes, R .
MATERIALS CHEMISTRY AND PHYSICS, 2000, 66 (01) :90-96
[2]  
Lebanowski J., 2005, ADV MAT SCI, V5, P14
[3]   Criteria for the evaluation of damage and remaining life in reformer furnace tubes [J].
LeMay, I ;
daSilveira, TL ;
Vianna, CH .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1996, 66 (1-3) :233-241
[4]  
*NAT MET LAB, 2006, 9302 CIEP2006SSP NAT
[5]  
*NAT MET LAB, 2001, CIEPSSP20010115 NAT
[6]  
*NAT MET LAB, 2000, CIEPSSP1999077 NAT M
[7]  
*NAT MET LAB, 2003, CIEPSSP20030141 NAT
[8]   Analysis of failed reformer tubes [J].
Ray, AK ;
Sinha, SK ;
Tiwari, YN ;
Swaminathan, J ;
Das, G ;
Chaudhuri, S ;
Singh, R .
ENGINEERING FAILURE ANALYSIS, 2003, 10 (03) :351-362
[9]  
SHARIAT MH, J CORR SCI ENG, V6
[10]   CREEP DAMAGE IN REFORMER TUBES [J].
SHIPLEY, DG .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1983, 14 (01) :21-34