Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salt

被引：76
作者：
Guo, Lei [1 ,2 ,3 ]
Zhang, Chenglong [1 ,2 ]
Li, Mingzhu [1 ,2 ]
Sun, Wei [1 ]
Zhang, Zhaoyang [1 ]
Ye, Fuxing [1 ,2 ,3 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, 92 Weijin Rd, Tianjin 300072, Peoples R China
[2] Tianjin Univ, Tianjin Key Lab Adv Joining Technol, 92 Weijin Rd, Tianjin 300072, Peoples R China
[3] Tianjin Univ, Key Lab Adv Ceram & Machining Technol, Minist Educ, 92 Weijin Rd, Tianjin 300072, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2017年 / 43卷 / 02期
基金：
中国国家自然科学基金;
关键词：
Thermal barrier coatings (TBCs); Doped YSZ; Hot corrosion; Molten salt; PHYSICAL VAPOR-DEPOSITION; ZIRCONIA COATINGS; PHASE-STABILITY; VANADATE SALT; EB-PVD; BEHAVIOR; YTTRIA; CERAMICS; SULFATE; RESISTANCE;
D O I：
10.1016/j.ceramint.2016.11.109
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
1 mol% Gd2O3 and 1 mol% Yb2O3 co-doped 3.5 mol% Y2O3 stabilized ZrO2 (GdYb-YSZ) ceramics in metastable tetragonal (t') structure were fabricated, and their hot corrosion behaviors were evaluated. The corrosion tests were performed at 700 degrees C, 800 degrees C, 900 degrees C and 1000 degrees C for 4 h in the presence of Na2SO4+V2O5 molten salt. After corrosion, t' phase could still be detected on the corroded surfaces and its content decreased with increasing the corrosion temperature. The corrosion products were composed of doped YVO4 and m-ZrO2, but some amounts of Na4V2O7 were found at low corrosion temperatures (700 degrees C and 800 degrees C). The corrosion resistance characteristic of GdYb-YSZ was compared with that of YSZ. Under an identical corrosion condition, GdYb-YSZ had less monoclinic phase formed, indicative of a better hot corrosion resistance. The hot corrosion mechanism was discussed in detail.
引用
收藏
页码：2780 / 2785
页数：6
相关论文
共 37 条
[1]   Hot Corrosion of Stabilized Zirconia Thermal Barrier Coatings and the Role of Mg Inhibitor [J].
Bajpai, Preeti ;
Das, Amit ;
Bhattacharya, Prajina ;
Madayi, Shimjith ;
Kulkarni, Kaustubh ;
Omar, Shobit .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2015, 98 (08) :2655-2661
[2]   Ceramic materials for thermal barrier coatings [J].
Cao, XQ ;
Vassen, R ;
Stoever, D .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (01) :1-10
[3]   Deposition mechanisms of yttria-stabilized zirconia coatings during plasma spray physical vapor deposition [J].
Gao, Lihua ;
Wei, Liangliang ;
Guo, Hongbo ;
Gong, Shengkai ;
Xu, Huibin .
CERAMICS INTERNATIONAL, 2016, 42 (04) :5530-5536
[4]   Microstructure and mechanical properties of yttria stabilized zirconia coatings prepared by plasma spray physical vapor deposition [J].
Gao, Lihua ;
Guo, Hongbo ;
Wei, Liangliang ;
Li, Chenyi ;
Gong, Shengkai ;
Xu, Huibin .
CERAMICS INTERNATIONAL, 2015, 41 (07) :8305-8311
[5]   Investigation on hot-fatigue behaviors of gradient thermal barrier coatings by EB-PVD [J].
Guo, HB ;
Gong, SK ;
Zhou, CG ;
Xu, HB .
SURFACE & COATINGS TECHNOLOGY, 2001, 148 (2-3) :110-116
[6]   Comparison of hot corrosion resistance of Sm2Zr2O7 and (Sm0.5Sc0.5)2Zr2O7 ceramics in Na2SO4+V2O5 molten salt [J].
Guo, Lei ;
Li, Mingzhu ;
Ye, Fuxing .
CERAMICS INTERNATIONAL, 2016, 42 (12) :13849-13854
[7]   Phase stability and thermal conductivity of RE2O3 (RE = La, Nd, Gd, Yb) and Yb2O3 co-doped Y2O3 stabilized ZrO2 ceramics [J].
Guo, Lei ;
Li, Mingzhu ;
Ye, Fuxing .
CERAMICS INTERNATIONAL, 2016, 42 (06) :7360-7365
[8]   Improved Toughness and Thermal Expansion of Non-stoichiometry Gd2-xZr2+xO7+x/2 Ceramics for Thermal Barrier Coating Application [J].
Guo, Lei ;
Li, Mingzhu ;
Zhang, Yu ;
Ye, Fuxing .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2016, 32 (01) :28-33
[9]   Thermal expansion and fracture toughness of (RE0.9Sc0.1)2Zr2O7 (RE=La, Sm, Dy, Er) ceramics [J].
Guo, Lei ;
Zhang, Yu ;
Zhao, Xiaoxiang ;
Wang, Caimei ;
Ye, Fuxing .
CERAMICS INTERNATIONAL, 2016, 42 (01) :583-588
[10]   The hot corrosion behavior of plasma sprayed zirconia coatings stabilized with yttria, ceria, and titania in sodium sulfate and vanadium oxide [J].
Habibi, M. H. ;
Guo, S. M. .
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (03) :270-277
1234