Evaluation and Optimization of the Mechanical Properties of Highly Filled PVC/(Wood Flour) Composites by Using Experimental Design

In this study, PVC/(wood flour) (WF) composites were prepared by using a counterrotating twin-screw extruder, and the effects on the mechanical properties of concentration and particle size of the WF, type and amount of coupling agent, K value of PVC, feed rate of extruder, and die temperature were investigated. Optimization of various formulation parameters based on the Taguchi method demonstrated that the wood content and wood particle size were the most important parameters. Flexural modulus increased upon increasing WF loading up to 50 wt%. Also, flexural strength and modulus increased with particle size because of the higher aspect ratio and better quality of mixing. Use of coupling agents had a minor effect that was attributed to the moderately high polarity of PVC causing relatively good compatibility between WF particles and the PVC matrix. The optimum level of WF calculated by considering the contribution factor was 50 wt%. J. VINYL ADDIT. TECHNOL., 17:112-119, 2011. (C) 2011 Society of Plastics Engineers