Use of Pluronic P103 Triblock Copolymer as Structural Agent during Synthesis of Hybrid Silver Nanoparticles

Dilute aqueous solutions of triblock copolymer Pluronic P103 were used to synthesize silver nanoparticles (Ag-NPs) by chemical reduction of silver nitrate (AgNO3) with sodium borohydride (NaBH4). This copolymer was used as a structural agent since monomers act as a stabilizer and micelles act as nanoreactors for nucleation and growth of Ag-NPs. The growth of the nanoparticles (NPs) was monitored by UV-visible spectroscopy on the basis of measuring surface plasmon resonance absorption over a temperature range of 25 to 70 degrees C. Shape and size of hybrid silver/P103 nanomaterials were tuned by varying the micellar structure of Pluronic P103 using a simple synthesis procedure. Dynamic Light Scattering (DLS) and Transmission Electron Microscopy (TEM) were used to study the size and shape of the hybrid nanomaterials. It was observed that Ag-NPs synthesized without Pluronic P103 at 25 degrees C exhibited a great variety of sizes. However, when Pluronic P103 was used below its critical micellar concentration (CMC), spherical-shaped Ag-NPs with uniform size were formed, suggesting that the copolymer had a stabilizing effect. On the other hand, when Ag-NPs were prepared with Pluronic P103 above the CMC, NPs with similar sizes as the micelles were detected, suggesting that the copolymer functioned as a nanoreactor. Furthermore, as temperature reached 35 degrees C, oval-shaped micelles were formed and small NPs were incorporated into the crown of the micelles. Independent Ag-NPs were not observed since they used the surface of the micelles as a soft template. Therefore, it was possible to obtain tiny Ag-NPs with homogeneous size.