Low level NO2 detection under humid background and associated sensing mechanism for mesoporous SnO2

Mesoporous SnO2 prepared by a hydrothermal synthesis route assisted by the ionic surfactant Cetyltrimethylammonium bromide, has rutile-type tetragonal symmetry, small homogeneous nanocrystallite size of similar to 4 nm and good thermal stability. Porosity analysis revealed high surface area similar to 127 m(2)/g and a narrow pore size distribution, with an average pore diameter similar to 4 nm. The mesoporous structure is likewise advantageous towards enhancing the surface reactivity and subsequent gas sensing performances. The role played by the surface hydroxylation on the NO2 sensing mechanism was discussed with respect to the associated photoelectron spectral components. Under humid air, associated with the in-field conditions, the highest sensitivity was attained at 150 degrees C, were the sensor signal towards NO2 is 4 times higher than the one recorded in dry air. This feature has been experimentally demonstrated by simultaneous electrical resistance and work function changes measurements conducted in the range of 400-5000 ppb NO2. (C) 2016 Elsevier B.V. All rights reserved.