Effect of double aging and microalloying on the age hardening behavior of a Mg-Sn-Zn alloy

被引：137
作者：
Sasaki, T. T. [1 ]
Oh-ishi, K. [1 ]
Ohkubo, T. [1 ]
Hono, K. [1 ]
机构：
[1] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050047, Japan
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2011年 / 530卷
关键词：
Mg-Sn alloy; Precipitation; Microalloying; Double aging; CREEP-BEHAVIOR; AS-CAST; PRECIPITATION; MICROSTRUCTURE; RESISTANCE; ADDITIONS; TENSILE; TEM;
D O I：
10.1016/j.msea.2010.05.010
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
We have investigated the effect of double aging and microalloying on the age hardening behavior of a Mg-2.2Sn-0.5Zn alloy. The double aging at 473 K after pre-aging at 343 K lead to an increased peak hardness to more than 80 HV as a result of the refinement of the polygonal Mg2Sn precipitates by the heterogeneous nucleation at densely dispersed MgZn2 precipitates. The age hardening response of the Mg-2.2Sn-0.5Zn alloy was further enhanced by microalloying with 0.2Cu (at.%), 0.2Ca-0.2Ag-0.2Zr or 1.0Al. In particular, the peak hardness of the Mg-2.2Sn-0.5Zn-1.0Al alloy was 95 HV at 433K. which was attributed to the synergy effect of the dispersion of the fine rod and polygonal Mg2Sn precipitates and solution hardening with Al. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：1 / 8
页数：8
相关论文
共 30 条
[1]  
[Anonymous], THESIS U TSUKUBA
[2]  
[Anonymous], MAGNESIUM TECHNOLOGY
[3]   TEM study of continuous precipitation in Mg-9 Wt%Al-l Wt%Zn alloy [J].
Celotto, S .
ACTA MATERIALIA, 2000, 48 (08) :1775-1787
[4]   PRECIPITATE STRENGTHENING MECHANISMS IN MAGNESIUM ZINC ALLOY SINGLE CRYSTALS [J].
CHUN, JS ;
BYRNE, JG .
JOURNAL OF MATERIALS SCIENCE, 1969, 4 (10) :861-&
[5]   TRANSMISSION ELECTRON MICROSCOPY STUDY OF AGE HARDENING IN A MG-5 WT PER CENT ZN ALLOY [J].
CLARK, JB .
ACTA METALLURGICA, 1965, 13 (12) :1281-&
[6]   Precipitation hardening in Mg-Zn-Sn alloys with minor additions of Ca and Si [J].
Cohen, S ;
Goren-Muginstein, G ;
Avraham, S ;
Rashkova, B ;
Dehm, G ;
Bamberger, M .
ZEITSCHRIFT FUR METALLKUNDE, 2005, 96 (09) :1081-1087
[7]   Precipitation- and stress-influenced coarsening in Mg-based Mg-Zn-Sn-Y and Mg-Zn-Sn-Sb alloys [J].
Gorny, Anton ;
Katsman, Alexander .
JOURNAL OF MATERIALS RESEARCH, 2008, 23 (05) :1228-1236
[8]   Microstructure and properties of Mg-5.6%Sn-4.4%Zn-2.1%Al alloy [J].
Harosh, S. ;
Miller, L. ;
Levi, G. ;
Bamberger, M. .
JOURNAL OF MATERIALS SCIENCE, 2007, 42 (24) :9983-9989
[9]   Microstructural investigations of the Mg-Sn-xCa system [J].
Hort, Norbert ;
Huang, Ybanding ;
Abu Leil, Torek ;
Maier, Petra ;
Kainer, Karl Ulrich .
ADVANCED ENGINEERING MATERIALS, 2006, 8 (05) :359-364
[10]   Effect of nano-particles on the creep resistance of Mg-Sn based alloys [J].
Kang, D. H. ;
Park, S. S. ;
Oh, Yoon S. ;
Kim, Nack J. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 449 :318-321
123