INFLUENCE OF PLASTIC DEFORMATION DURING EXTRUSION PROCESS ON HEAT RESISTANCE ALLOYS Fe40Al

The article presents the results of studies on the effects wrought on the corrosion resistance of the alloy matrix phase intermetallic FeAl. Researches were carried out on the Fe40Al5Cr0.2TiB alloy and involved the oxidation of the samples after the crystallization after plastic deformation made by extrusion. The tests were performed in an oven in air at 1100 degrees C for 100, 300 and 500 h. Determined to change the mass of the samples after corrosion research setting kinetics of corrosion processes, as well as an analysis of the microstructure of the alloy after the crystallization and after forming. The structure was examined using light microscopy and scanning electron microscopy and X-ray microanalysis with EDS chemical composition of the corrosion products. The test results revealed that plastic deformation during extrusion of intermetallic alloy led to structural changes, the effect of which was to improve the heat resistance at a temperature of 1100 degrees C.