The Effect of Aluminum Oxide (Al2O3) and Cerium Oxide (CeO2) on the Structural and Mechanical Properties of Yttria Tetragonal Zirconia Polycrystal (Y-TZP)

被引：0

作者：

Golieskardi, M. ^{[1
]}

Satgunam, M. ^{[1
]}

Ragurajan, D. ^{[1
]}

Ansari, M. N. M. ^{[1
]}

机构：

[1] Univ Tenaga Nas, Ctr Adv Mat, Kajang 43000, Selangor, Malaysia

来源：

JOURNAL OF THE AUSTRALIAN CERAMIC SOCIETY | 2015年 / 51卷 / 01期

关键词：

Aluminum Oxide; Cerium Oxide; sintering behavior; Y-TZP; Mechanical Properties; LOW-TEMPERATURE DEGRADATION; BIOMEDICAL-GRADE ZIRCONIA; FRACTURE-RESISTANCE; CERAMICS; TRANSFORMATION; WATER; AIR;

D O I：

暂无

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of additions of Al2O3 and CeO2 (up to 1 wt %) on the sintering behavior of yttria-stabilized Tetragonal Zirconia Polycrystals (Y-TZP) were studied. The effects of Al2O3 and CeO2 on the Vickers hardness, bulk density, fracture toughness and Young's modulus were carried out on the sintered samples. The sintering temperature was ranging from 1250 degrees C to 1450 degrees C with the ramp rate of 10 degrees C/min. The results revealed that the doped samples demonstrated a stronger effect in contrast with the undoped samples. The relative densities were above 97.5 % of theoretical (i.e. > 6.1 gcm(-3)) could be obtained in Y-TZPs sintered at low temperatures, 1350 degrees C. The hardness's value of Y-TZP was increased in the 1 wt % Al2O3 and CeO2-doped samples when sintered above 1400 degrees C.

引用

页码：16 / 21

页数：6

共 31 条

[1]

[Anonymous], 2000, 14705 ISO

[2]

*ASTM, 1999, E38499 ASTM

[3] THE EFFECT OF CERIA CO-DOPING ON CHEMICAL-STABILITY AND FRACTURE-TOUGHNESS OF Y-TZP [J].

BOUTZ, MMR ;

WINNUBST, AJA ;

VANLANGERAK, B ;

SCHOLTENHUIS, RJMO ;

KREUWEL, K ;

BURGGRAAF, AJ .

JOURNAL OF MATERIALS SCIENCE, 1995, 30 (07) :1854-1862

[4] ANCHORAGE OF THE FEMORAL HEAD PROSTHESIS TO THE SHAFT OF THE FEMUR [J].

CHARNLEY, J .

JOURNAL OF BONE AND JOINT SURGERY-BRITISH VOLUME, 1960, 42 (01) :28-30

[5] STERILE-AIR OPERATING THEATRE ENCLOSURE [J].

CHARNLEY, J .

BRITISH JOURNAL OF SURGERY, 1964, 51 (03) :195-&

[6] The processing-related fracture resistance and reliability of root dental posts made from Y-TZP [J].

Dakskobler, Ales ;

Jevnikar, Peter ;

Oblak, Cedomir ;

Kosmac, Tomaz .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (2-3) :1565-1570

[7] Influence of surface finish and residual stresses on the ageing sensitivity of biomedical grade zirconia [J].

Deville, S ;

Chevalier, J ;

Gremillard, L .

BIOMATERIALS, 2006, 27 (10) :2186-2192

[8]

Gakovic L., 2007, U. S. Patent, Patent No. [7. 214,046., 7214046]

[9]

German R., 2006, SINTERING THEORY PRA, V11, P568

[10] Modeling the aging kinetics of zirconia ceramics [J].

Gremillard, L ;

Chevalier, J ;

Epicier, T ;

Deville, S ;

Fantozzi, G .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (13) :3483-3489

← 1 2 3 4 →