Enhanced hydrophilicity and antifouling performance of PES-C/emodin ultrafiltration membrane

In this article, an ultrafiltration membrane was fabricated from phenolphthalein polyethersulfone (PES-C) modified with emodin using a phase-inversion method. ATR-FTIR and UV-vis analysis showed that emodin had good compatibility with the PES-C ultrafiltration membrane. SEM showed that the prepared ultrafiltration membranes consisted of a porous skin layer and a macroporous support sublayer. The contact angle value of the pure PES-C ultrafiltration membrane was 77.71 degrees and that of the PES-C ultrafiltration membrane blended with 0.105 wt.% emodin decreased to 65.71 degrees, which explained the fact why its pure water flux significantly increased from 190 L/m(2)center dot h to 387 L/m(2)center dot h. The antifouling properties of the obtained ultrafiltration membranes were assessed by static protein adsorption, bacterial adhesion, antibacterial tests, and filtration experiments with BSA. The PES-C (13.895 wt.%)/emodin (0.105 wt.%) ultrafiltration membrane presented the lowest protein adsorption rate (1.44%), the highest flux recovery ratio (57%), and the largest inhibition zone diameter (3.0 +/- 0.06 mm). Compared with that of the pure PES-C ultrafiltration membrane, the bacterial adhesion effect of the PES-C/emodin (0.105 wt.%) ultrafiltration membrane was significantly reduced. In addition, PES-C incorporated into the emodin ultrafiltration membrane had excellent stability in a deionized water system.