Effect of Hyperbranched Poly (Trimellitic Anhydride Ethylene Glycol) Epoxy (HTME) on Thermal Degradation Activation Energies of HTME/Diglycidyl Ether of Bisphenol-A Epoxy Hybrid Resin by Kissinger and Flynn-Wall-Ozawa Method

The thermal degradation behavior and kinetics of hyperbranched poly (trimellitic anhydride ethylene glycol) epoxy (HTME)/diglycidyl ether of bisphenol-A epoxy (DGEBA) hybrid resin was investigated with thermogravimetric analysis (TGA) by using Kissinger method and Flynn-Wall-Ozawa method. The results show that the thermal degradation activation energies of DGEBA, 9 wt% HTME-1/91wt% DGEBA, 3 wt% HTME-2/97 wt% DGEBA, 9 wt% HTME-2/91 wt% DGEBA, 15 wt% HTME-2/85 wt% DGEBA, and 9wt% HTME-3/91wt% DGEBA are 152.5, 144.4, 135.4, 133.2, 121.8 and 143.0 kJmol(-1), respectively, by Kissinger method. and the activation energies are 173.3, 165.0, 163.2, 151.7, 137.7 and 159.7 kJmol(-1), respectively by Flynn-Wall-Ozawa method. With the increase of HTME content, the activation energies of HTME/DGEBA hybrid resin decrease. Although molecular weight or generation of hyperbranched epoxy resins (HTME) has little effect on the thermal degradation activation energies and other kinetics data.