Preparation, Mechanical and Electrical Properties of Glass and Jute-Epoxy/Epoxy Polyurethane Composites

被引：14

作者：

Adroja, Pooja P. ^{[1
]}

Koradiya, S. B. ^{[1
]}

Patel, J. P. ^{[2
]}

Parsania, P. H. ^{[1
]}

机构：

[1] Saurashtra Univ, Dept Chem, Div Polymer Chem, Rajkot 360005, Gujarat, India

[2] SP Univ, Dept Chem, Vv Nagar, Gujarat, India

来源：

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING | 2011年 / 50卷 / 09期

关键词：

Epoxy polyurethane; Epoxy resin; Fiber surface modification; Mechanical and electrical properties; HYBRID COMPOSITES; PERFORMANCE EVALUATION; PHYSICAL-PROPERTIES; ALKALI; RESIN; FIBERS;

D O I：

10.1080/03602559.2011.553860

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Glass and jute (treated and untreated) composites of epoxy resin of 1,1'-bis(3-methyl-4-hydroxy phenyl)cyclohexane(EMC) cured using 20% triethylamine as a hardener (G-EMCT-20 and J-EMCT-20) and EMC- polyurethane of toluene diisocyanate (J-EMCPU and TJ-EMCPU) have been prepared by a hand layup technique under 27.58MPa pressure and at 150 degrees C for 4h. G-EMCT-20, J-EMCT-20, J-EMCPU and TJ-EMCPU showed 275, 96.5, 37.3 and 31.5MPa tensile strength; 351, 84, 10 and 24MPa flexural strength; 5837, 2758, 1277 and 1619MPa elastic modulus; 24.6, 7.1, 1.9 and 1.6kV/mm electric strength; and 1.4x1013, 1.1x1011, 7.7x1010 and 3.6x1010ohmcm volume resistivity, respectively. Fairly good to excellent mechanical and electrical properties of the composites indicated their industrial applications in building and construction, electrical and electronic industries.

引用

页码：937 / 940

页数：4

共 30 条

[1] Synthesis, Curing Behavior and Characterization of Epoxyacrylate and Triethylamine Cured Epoxy Resin of 1,1′-Bis(3-methyl-4-hydroxy phenyl) cyclohexane [J].

Adroja, Pooja P. ;

Kporadiya, S. B. ;

Parsania, P. H. .

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2011, 50 (01) :52-58

[2] Immersion temperature effects on the water absorption behavior of hybrid lignocellulosic fiber reinforced-polyester matrix composites [J].

Alsina, O. L. S. ;

de Carvalho, L. H. ;

Ramos Filho, F. G. ;

d'Almeida, J. R. M. .

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2007, 46 (05) :515-520

[3]

Baraiya R, 1997, INT J POLYM MATER, V38, P1, DOI DOI 10.1080/00914039708031490

[4]

Baraiya R, 1998, INT J POLYM MATER, V39, P255, DOI DOI 10.1080/00914039808039772

[5] THE EFFECT OF SILANE TREATMENT ON THE MECHANICAL AND PHYSICAL-PROPERTIES OF SISAL-EPOXY COMPOSITES [J].

BISANDA, ETN ;

ANSELL, MP .

COMPOSITES SCIENCE AND TECHNOLOGY, 1991, 41 (02) :165-178

[6] Instrumented impact testing of kenaf fiber reinforced polypropylene composites: effects of temperature and composition [J].

Clemons, Craig ;

Sanadi, Anand R. .

JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2007, 26 (15) :1587-1602

[7]

Drzal L.T., 2004, NSF-PATH Housing Research Agenda, V2, P129

[8]

Johari G.P., 1993, CHEM TECHNOLOGY EPOX

[9] Studies on acrylonitrile-butadiene (NBR) latex-reinforced jute nonwoven fabric composites: Chemical resistance, mechanical properties, and water absorption [J].

Kumar, MNS ;

Siddaramaiah .

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2006, 45 (03) :409-414

[10] Preparation of epoxy resin/silica hybrid composites for epoxy molding compounds [J].

Liu, YL ;

Lin, YL ;

Chen, CP ;

Jeng, RJ .

JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 90 (14) :4047-4053

← 1 2 3 →