Effect of final annealing temperature on critical current density of Ag/Bi-(Pb)-Sr-Ca-Cu-O tapes

被引：4

作者：

Liu, HK ^{[1
]}

Bhasale, R ^{[1
]}

Guo, YC ^{[1
]}

Horvat, J ^{[1
]}

Zeimetz, B ^{[1
]}

Dou, SX ^{[1
]}

机构：

[1] Univ Wollongong, Ctr Supercond & Elect Mat, Wollongong, NSW 2522, Australia

来源：

APPLIED SUPERCONDUCTIVITY | 1997年 / 5卷 / 1-6期

基金：

澳大利亚研究理事会;

关键词：

D O I：

10.1016/S0964-1807(98)00022-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A two-stage annealing procedure in the final thermal cycle has been tested for processing Ag/Bi:2223 tapes. The effect of various annealing temperatures in the final stage of heat treatment on phase transition, microstructure and critical current (I-c) was investigated for Ag/Bi:2223 tapes. It was found that annealing at higher temperatures (835-845 degrees C) leads to a relatively purer Bi:2223 phase but a small fraction of Bi:2201 always coexists with Bi:2223. Whereas annealing at lower temperatures (800-825 degrees C) results in conversion of Bi:2201 to Bi:2212 and possibly partial decomposition of Bi:2223. I-c was reduced to half for tapes annealed at 835-845 degrees C due to the presence of' Bi:2201, compared with tapes annealed at low temperatures. Scanning electron microscopy (SEM) studies Show that, although the amount of Bi:2201 is small, it resides along the Bi:2223 colony boundaries, blocking the current flow between colonies. The drastic weak link effect of Bi:2201 is attributable to the combination of the elongated platelike morphology and insulating property. (C) 1998 Published by Elsevier Science Ltd. All rights reserved.

引用

页码：171 / 177

页数：7

共 17 条

[1] ENHANCED FLUX PINNING THROUGH A PHASE FORMATION- DECOMPOSITION-RECOVERY PROCESS IN AG-SHEATHED Bi(Pb)SrCaCuO WIRES [J].

Dou, S. X. ;

Liu, H. K. ;

Guo, Y. C. ;

Shi, D. L. .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1993, 3 (01) :1135-1138

[2] IMPROVEMENT OF FLUX PINNING IN THE AG-CLAD BI-PB-SR-CA-CU-O WIRES THROUGH THE USE OF A SHORT-PERIOD MELT PROCESSING [J].

DOU, SX ;

LIU, HK ;

GUO, YC .

APPLIED PHYSICS LETTERS, 1992, 60 (23) :2929-2931

[3] AG-SHEATHED BI(PB)SRCACUO SUPERCONDUCTING TAPES [J].

DOU, SX ;

LIU, HK .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1993, 6 (05) :297-314

[4]

Eibl O., 1994, Proceedings of the 7th International Workshop on Critical Currents in Superconductors, P27

[5]

FENG Y, 1994, INTERFACE SCI, V1, P401

[6] STABILITY OF HIGH-TC PHASE IN AG-CLAD BI-BASED SUPERCONDUCTING WIRES [J].

GUO, YC ;

LIU, HK ;

DOU, SX .

PHYSICA C, 1992, 200 (1-2) :147-154

[7] EFFECT OF A CONTROLLED MELT PROCESS ON PHASE-TRANSFORMATION AND ELECTROMAGNETIC PROPERTIES OF BIPBSRCACUO/AG SUPERCONDUCTING WIRES [J].

GUO, YC ;

LIU, HK ;

DOU, SX .

APPLIED SUPERCONDUCTIVITY, 1993, 1 (1-2) :25-31

[8]

GUO YC, 1993, MAT SCI ENG B-SOLID, V193, P63

[9]

GUO YC, 1997, IN PRESS PHYSICA C

[10] MICROSTRUCTURE AND DEFECTS IN AG-CLAD BI-PB-SR-CA-CU-O WIRES PREPARED THROUGH A CONTROLLED MELT PROCESS [J].

LIU, HK ;

GUO, YC ;

DOU, SX .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1992, 5 (10) :591-598

← 1 2 →