High-dose neutron irradiation of MgAl2O4 spinel:: effects of post-irradiation thermal annealing on EPR and optical absorption

被引：30

作者：

Ibarra, A

Bravo, D

Lopez, FJ

Garner, FA

机构：

[1] CIEMAT Fus Assoc, EURATOM, Inst Invest Basica, E-28040 Madrid, Spain

[2] Univ Autonoma Madrid, Dept Fis Mat, Fac Ciencias C 4, E-28049 Madrid, Spain

[3] Pacific NW Natl Lab, Richland, WA USA

来源：

JOURNAL OF NUCLEAR MATERIALS | 2005年 / 336卷 / 2-3期

关键词：

D O I：

10.1016/j.jnucmat.2004.09.003

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Electron paramagnetic resonance (EPR) and optical absorption spectra were measured during thermal annealing of stoichiometric MgAl2O4 spinel that was previously irradiated in the Materials Open Test Assembly in the Fast Flux Test Facility (FFTF/MOTA) at approximate to 680 K to;approximate to 50 dpa. Both F and F+ centres are to persist up to very high temperatures (over 1000K) suggesting the operation of an annealing mechanism controlled by the thermal stability of extended defects. Using X-ray irradiation following the different annealing steps it was shown that an optical absorption band at 37000cm(-1) is related to a sharp EPR band at g = 2.0005 and that the defect causing these effects is the F+ centre. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：156 / 162

页数：7