Integration of H2 barriers for ferroelectric memories based on SrBi2Ta2O9 (SBT)

被引:8
|
作者
Hartner, W [1 ]
Schindler, G [1 ]
Bosk, P [1 ]
Gabric, Z [1 ]
Kastner, M [1 ]
Beitel, G [1 ]
Mikolajick, T [1 ]
Dehm, C [1 ]
Mazuré, C [1 ]
机构
[1] Infineon Technol AG, D-81730 Munich, Germany
关键词
ferroelectrics; SBT; SrBi2Ta2O9; encapsulation; hydrogen; top electrode;
D O I
10.1080/10584580008215660
中图分类号
TM [电工技术]; TN [电子技术、通信技术];
学科分类号
0808 ; 0809 ;
摘要
In this study, integration of an hydrogen barrier into a FeRAM process flow is investigated. It is reported in the literature that ferroelectric properties can be maintained after hydrogen annealing by using IrOx as a top electrode [16][17][18]. Advantage of materials like IrOx is less catalytic activity compared to Pt. However, we found that IrOx is not a promising candidate for top electrode barrier. (Pt)/IrOx/SBT/Pt capacitors are prone to shorting or exhibit high leakage. IrOx films are very easily reduced by reducing ambient which will result in peeling off. Also, IrOx films tend to oxidize Ti or TiN layers immediately. Therefore, other barrier materials or layer sequences like Ir/IrOx have to be considered. For protection of the entire capacitor an Encapsulation Barrier Layer (EBL) is required. In this study, LPCVD SiN is used. LPCVD SiN is a standard material in CMOS technology. Production tools are available and it is well known as hydrogen barrier. By modifying the deposition process and using a novel process sequence, no visual damage of the capacitors after SiN-deposition and FGA is seen. Also, no degradation of electrical properties after capacitor formation as well as after SiN-deposition and FGA is observed. However, after metal 1 and metal 2 processing, 2P(r) values at 1.8V are reduced from 12 muC/cm(2) to 2 muC/cm(2). Polarization at 5.0V is not affected.
引用
收藏
页码:273 / 284
页数:12
相关论文
共 50 条
  • [21] Phase transition in ferroelectric SrBi2Ta2O9 single crystal
    Yoshio, K
    Matsubara, I
    Yamada, A
    Onodera, A
    Sakai, A
    Yamashita, H
    JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 2003, 42 : S1034 - S1037
  • [22] Electronic structure of the layered ferroelectric perovskite SrBi2Ta2O9
    Robertson, J
    Chen, CW
    Warren, WL
    FERROELECTRIC THIN FILMS V, 1996, 433 : 279 - 284
  • [23] Electronic structure of the ferroelectric layered perovskite SrBi2Ta2O9
    Cambridge Univ, Cambridge, United Kingdom
    Appl Phys Lett, 12 (1704-1706):
  • [24] Structural phase transitions in the ferroelectric oxide SrBi2Ta2O9
    Macquart, R
    Kennedy, BJ
    Hunter, BA
    Howard, CJ
    Shimakawa, Y
    INTEGRATED FERROELECTRICS, 2002, 44 : 101 - 112
  • [25] Synthesis and characterization of ferroelectric SrBi2Ta2O9 nanotubes arrays
    Ming Feng
    Wen Wang
    Yu Zhou
    Dechang Jia
    Journal of Sol-Gel Science and Technology, 2009, 52 : 120 - 123
  • [26] Sintering behavior of SrBi2Ta2O9 layered ferroelectric ceramics
    Chen, YC
    Lu, CH
    DIELECTRIC CERAMIC MATERIALS, 1999, 100 : 217 - 225
  • [27] Soft phonon and bismuth content in ferroelectric SrBi2Ta2O9
    Kojima, Seiji
    Saitoh, Itaru
    Physica B: Condensed Matter, 1999, 263 : 653 - 656
  • [28] Defect chemistry of SrBi2Ta2O9 and ferroelectric fatigue endurance
    Palanduz, AC
    Smyth, DM
    JOURNAL OF ELECTROCERAMICS, 2000, 5 (01) : 21 - 30
  • [29] Electronic structure of the ferroelectric layered perovskite SrBi2Ta2O9
    Robertson, J
    Chen, CW
    Warren, WL
    Gutleben, CD
    APPLIED PHYSICS LETTERS, 1996, 69 (12) : 1704 - 1706
  • [30] Soft phonon and bismuth content in ferroelectric SrBi2Ta2O9
    Kojima, S
    Saitoh, I
    PHYSICA B, 1999, 263 : 653 - 656