Effect of W addition on compressive strength of Nb-10Mo-10Ti-18Si-Base in-situ composites

被引:15
作者
Sha, JB [1 ]
Hirai, H [1 ]
Tabaru, T [1 ]
Kitahara, A [1 ]
Ueno, H [1 ]
Hanada, S [1 ]
机构
[1] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
来源
MATERIALS TRANSACTIONS JIM | 2000年 / 41卷 / 09期
关键词
refractory metal-intermetallic composites; niobium solid solution; niobium silicide; arc casting; directional solidification; Vickers hardness; high-temperature compressive strength;
D O I
10.2320/matertrans1989.41.1125
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Niobium solid solution/niobium silicides in-situ composites are expected to have applications in the future as high-temperature structural materials. To improve the high temperature strength further, we tried to add tungsten to Nb-10Mo-10Ti-18Si eutectic alloy by replacing Nb with 0, 5, 10 and 15 mol%W. The samples were prepared by are casting and some of them were directionally solidified by the floating zone melting technique at a growth rate of 15 mm/h. After annealing at 1870 K for 100 h, the microstructure? Vickers hardness and high-temperature compressive strength were examined. The samples without W consisted of eutectic Nb solid solution and (Nb, Mo, Ti)(5)Si-3 silicide, while primary Nb solid solution appeared as a result of substituting W for Nb. The microstructure of directionally solidified samples was coarse and oriented in the direction of growth, but they did not show the typical microstructure often observed in the case of directionally solidified materials. The Vickers hardness increased with increasing W content. The 0.2% yield strength (sigma (0.2)) and the specific 0.2% yield strength (sigma (0.2S)) (sigma (0.2) divided by the density) at 1670 K increased markedly with increasing W content. The directionally solidified samples showed higher sigma (0.2) and sigma (0.2S) than the are-cast samples. Even at 1770 K, the directionally solidified sample with 15 mol% W showed sigma (0.2) of about 650 MPa.
引用
收藏
页码:1125 / 1128
页数:4
相关论文
共 12 条
[1]  
BEGLEY RT, 1994, EVOLUTION OF REFRACTORY METALS AND ALLOYS, P29
[2]   Refractory metal intermetallic in-situ composites for aircraft engines [J].
Bewlay, BP ;
Lewandowksi, JJ ;
Jackson, MR .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1997, 49 (08) :44-+
[3]  
ERICKSON GL, 1995, JOM-J MIN MET MAT S, V47, P36
[4]   Microstructures and mechanical properties of directionally solidified Nb-xMo-22Ti-18Si in-situ composites [J].
Hirai, H ;
Tabaru, T ;
Ueno, H ;
Kitahara, A ;
Hanada, S .
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2000, 64 (06) :474-480
[5]  
Jackson MR, 1996, JOM-J MIN MET MAT S, V48, P39
[6]   STRENGTH AND TOUGHNESS OF A NB/NB5SI3 COMPOSITE [J].
MENDIRATTA, MG ;
DIMIDUK, DM .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1993, 24 (02) :501-504
[7]   STRENGTH AND DUCTILE-PHASE TOUGHENING IN THE 2-PHASE NB/NB5SI3 ALLOYS [J].
MENDIRATTA, MG ;
LEWANDOWSKI, JJ ;
DIMIDUK, DM .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (07) :1573-1583
[8]   Phase transformations in Nb-Al-Ti alloys [J].
Menon, ESK ;
Subramanian, PR ;
Dimiduk, DM .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (06) :1647-1659
[9]   Microstructures and mechanical properties of Nb-Mo-Ti-Si-C in-situ composites prepared by arc melting and directional solidification [J].
Sha, JB ;
Hirai, H ;
Tabaru, T ;
Kitahara, A ;
Ueno, H ;
Hanada, S .
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2000, 64 (05) :331-334
[10]  
Subramanian PR, 1996, JOM-J MIN MET MAT S, V48, P33