Properties of acrylic resin/nano-SiO2 leather finishing agent prepared via emulsifier-free emulsion polymerization

被引：74
作者：
Hu, Jing [1 ]
Ma, Jianzhong [1 ]
Deng, Weijun [1 ]
机构：
[1] Shaanxi Univ Sci & Technol, Coll Resource & Environm, Xian 710021, Shaanxi, Peoples R China
来源：
MATERIALS LETTERS | 2008年 / 62卷 / 17-18期
基金：
中国国家自然科学基金;
关键词：
polymer; nanocomposites; emulsifier-free emulsion; leather;
D O I：
10.1016/j.matlet.2008.01.127
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Acrylic resin/nano-SiO2 leather finishing agent was prepared via emulsifier-free emulsion polymerization. Fourier Transform Infrared Spectroscopy (FT-IR) indicated that the structure of acrylic resin/nano-SiO2. Dynamics Laser Scattering (DLS) indicated that the average diameter of acrylic resin/nano-SiO2 (155.5 nm) was bigger than pure acrylic resin (97.7 nm) and correspondingly zeta potential decreased. Differential Scanning Calorimeters (DSC) analysis showed that the glass transition temperature (Tg) of the EFAR/SiO2 (Tg=- 18.2 degrees C) was higher than that of EFAR (Tg= -23.6 degrees C). Moreover, in contrast to acrylic resin, the applied properties of the leather finished by the acrylic resin/nano-SiO2 were measured: water vapor permeability increased by 7.80% as well as water uptake decreased by 17.89%. (C) 2008 Elsevier B.V. All rights reserved.
引用
收藏
页码：2931 / 2934
页数：4
相关论文
共 27 条
  • [1] The acrylic resin leather coating agent modified by nano-SiO2
    Ma, Jianzhong
    Hu, Jing
    Zhang, Zhijie
    Liu, Lingyun
    JOURNAL OF COMPOSITE MATERIALS, 2006, 40 (24) : 2189 - 2201
  • [2] Structure and Properties of Nano-SiO2/Acrylic Composite Emulsion with Interpenetrating Networks Prepared via Soap-Free Emulsion Polymerization
    Chen, Lijun
    Shi, Hongxin
    JOURNAL OF DISPERSION SCIENCE AND TECHNOLOGY, 2010, 31 (04) : 466 - 470
  • [3] Synthesis and characterization of organic fluorine and nano-SiO2 modified polyacrylate emulsifier-free latex
    Zhou, Jianhua
    Chen, Xin
    Duan, Hao
    Ma, Jianzhong
    PROGRESS IN ORGANIC COATINGS, 2015, 89 : 192 - 198
  • [4] Synthesis of polystyrene-silica nanoparticles via RAFT emulsifier-free emulsion polymerization
    Tumnantong, Dusadee
    Rempel, Garry L.
    Prasassarakich, Pattarapan
    EUROPEAN POLYMER JOURNAL, 2016, 80 : 145 - 157
  • [5] Polyacrylate/silica hybrids prepared by emulsifier-free emulsion polymerization and the sol–gel process
    Yi-Ding Shen
    Yan-Na Zhao
    Xiao-Rui Li
    Polymer Bulletin, 2009, 63 : 687 - 698
  • [6] Preparation of BA/ST/AM nano particles by ultrasonic emulsifier-free emulsion polymerization
    Yin, NW
    Chen, KQ
    Kang, W
    ULTRASONICS SONOCHEMISTRY, 2006, 13 (04) : 345 - 351
  • [7] Polyacrylate/silica hybrids prepared by emulsifier-free emulsion polymerization and the sol-gel process
    Shen, Yi-Ding
    Zhao, Yan-Na
    Li, Xiao-Rui
    POLYMER BULLETIN, 2009, 63 (05) : 687 - 698
  • [8] Nano-SiO2/PMMA-PU composite particles with core- shell structure via emulsion polymerization and their application in epoxy resin
    Huang, Zeng Fang
    Qu, Xiao Yue
    Chen, Zheng
    JOURNAL OF APPLIED POLYMER SCIENCE, 2015, 132 (19)
  • [9] Polyisoprene-Silica Nanoparticles Synthesized via RAFT Emulsifier-Free Emulsion Polymerization Using Water-Soluble Initiators
    Tumnantong, Dusadee
    Rempel, Garry L.
    Prasassarakich, Pattarapan
    POLYMERS, 2017, 9 (11):
  • [10] Polystyrene/nano-SiO2 composite microspheres fabricated by Pickering emulsion polymerization: Preparation, mechanisms and thermal properties
    Zhang, W. H.
    Fan, X. D.
    Tian, W.
    Fan, W. W.
    EXPRESS POLYMER LETTERS, 2012, 6 (07): : 532 - 542
123