Nitride Dispersion Strengthened Steel Development after Sintering of Nitrided Fe-4.6 at% Al Alloy Powder

被引:5
作者
Yadav, Akeshwar Singh [1 ]
Kuernsteiner, Philipp [2 ,3 ]
Jaegle, Eric A. [2 ,4 ]
Sasidhar, K. N. [1 ,2 ]
Meka, Sai Ramudu [1 ]
机构
[1] Indian Inst Technol Roorkee IIT Roorkee, Dept Met & Mat Engn, Roorkee 247667, India
[2] Max Planck Inst Eisenforsch GmbH, Dept Microstruct Phys & Alloy Design, D-40237 Dusseldorf, Germany
[3] Johannes Kepler Univ Linz, Ctr Surface & Nanoanalyt, Christian Doppler Lab Nanoscale Phase Transformat, Linz Altenberger Str 69, A-4040 Linz, Austria
[4] Univ Bundeswehr Munchen, Inst Mat Sci, D-85577 Neubiberg, Germany
关键词
aluminum nitride; ferritic iron; nitride dispersion; spark plasma sintering; X-RAY; IRON; OXIDE; PRECIPITATION; ALUMINUM; DENSITY;
D O I
10.1002/srin.202100174
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The development of a composite microstructure with hard aluminum nitrides (AlN) dispersed in a soft ferritic iron-based solid is achieved through the powder metallurgy route. Fe-4.6 at% Al alloy powders subjected to two different thermochemical treatments viz. nitriding and nitriding followed by hydrogen reduction are consolidated by spark plasma sintering (SPS) at 900 degrees C. The final sintered microstructure is characterized with the help of optical, scanning electron, and transmission electron microscopy along with X-ray diffraction for detailed phase analysis. The microstructures of the nitrided and sintered compacts are observed to be significantly affected by two factors: 1) presence of oxide phases on the surface of the powder particles before SPS and 2) evolution of nitrogen gas due to dissociation of iron nitrides during sintering. These result in a very complicated microstructure. However, for nitrided powders, performing a hydrogen reduction step before SPS lead to a microstructure composed of precipitation-hardened particle cores due to dispersion of nanosized AlN precipitates, with a soft, ferritic interparticle region. This composite microstructure achieved through the powder metallurgy route, which can be finely tuned by controlling the nitriding, oxidation, and sintering parameters, is envisioned to be greatly beneficial for several engineering applications such as automotive components.
引用
收藏
页数:11
相关论文
共 38 条
[1]   Lattice-parameter change induced by accommodation of precipitate/matrix misfit; misfitting nitrides in ferrite [J].
Akhlaghi, M. ;
Steiner, T. ;
Meka, S. R. ;
Leineweber, A. ;
Mittemeijer, E. J. .
ACTA MATERIALIA, 2015, 98 :254-262
[2]   Precipitates in aluminium alloys [J].
Andersen, Sigmund J. ;
Marioara, Calin D. ;
Friis, Jesper ;
Wenner, Sigurd ;
Holmestad, Randi .
ADVANCES IN PHYSICS-X, 2018, 3 (01) :790-813
[3]   THE KINETICS OF THE INTERNAL NITRIDING OF FE-2 AT PCT AL-ALLOY [J].
BIGLARI, MH ;
BRAKMAN, CM ;
MITTEMEIJER, EJ ;
VANDERZWAAG, S .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1995, 26 (04) :765-776
[4]  
Callister W.D., 2007, MAT SCI ENG IN INTRO
[5]   Current state of Fe-Mn-Al-C low density steels [J].
Chen, Shangping ;
Rana, Radhakanta ;
Haldar, Arunansu ;
Ray, Ranjit Kumar .
PROGRESS IN MATERIALS SCIENCE, 2017, 89 :345-391
[6]   LATTICE-PARAMETERS OF IRON-CARBON AND IRON-NITROGEN MARTENSITES AND AUSTENITES [J].
CHENG, L ;
BOTTGER, A ;
DEKEIJSER, TH ;
MITTEMEIJER, EJ .
SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (03) :509-514
[7]  
Cullity B. D., ELEMENTS XRAY DIFFRA
[8]   Development of strong, oxidation and corrosion resistant nickel-based superalloys: critical review of challenges, progress and prospects [J].
Darolia, R. .
INTERNATIONAL MATERIALS REVIEWS, 2019, 64 (06) :355-380
[9]  
Davis J. R., 1993, Aluminum and aluminum alloys
[10]  
Deiter G.E., 2013, MECH METALLURGY SI M