Crystal growth of melt-textured Nd-123 under 1% oxygen partial pressure atmosphere

Crystal growth of melt-textured Nd-123 pseudocrystals was investigated via an isothermal solidification with top-seeding technique under a 1%O-2 in N-2 atmosphere. Nonsteady state solidification was observed at low undercooling, in contrast to an almost linear growth at higher undercooling, Similar to processing in air, the substitution of Nd/Ba was found to decrease from the seed position to the edge of the crystal. In addition, the volume fraction of Nd-422 particles decreased in the solid as solidification proceeded. As a result of these microstructural inhomogeneities, the critical temperature and the critical current density varied within the crystal even for samples processed isothermally, despite the narrow solid solution range of the Nd-123 phase under a reduced pO(2) atmosphere.