Role of rare-earth elements in glass formation of Al-Ca-Ni amorphous alloys

被引：16

作者：

Chen, Z. P. ^{[1
]}

Gao, J. E. ^{[1
]}

Wu, Y. ^{[1
]}

Li, H. X. ^{[1
]}

Wang, H. ^{[1
]}

Lu, Z. P. ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2012年 / 513卷

基金：

中国国家自然科学基金;

关键词：

Glass forming-ability; RE elements; Atom size difference; BULK METALLIC GLASSES; FORMING ABILITY; CO; ALUMINUM; SYSTEMS;

D O I：

10.1016/j.jallcom.2011.10.054

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Effects of different rare-earth (RE) elements (i.e., Y, Ce, La and Yb) on the glass forming-ability (GFA) of Al-Ca-Ni alloy system were systematically investigated. The optimum addition content of all the four RE is 1 at.% and ytterbium is the most effective as far as the GFA is considered. Our analysis confirmed that proper additions of Yb could not only impede the formation of the competing alpha-Al clusters, but also enhance the liquid stability (i.e., lower the liquidus temperature). Although additions of Y, Ce and La in the Al88Ca7Ni5 can also retard the alpha-Al precipitation, nevertheless, it seemed that their large atomic size difference with Ca could destabilize the original liquid stability (i.e., increase the liquidus temperature). (C) 2011 Elsevier B. V. All rights reserved.

引用

页码：387 / 392

页数：6

共 18 条

[11] Discovering inch-diameter metallic glasses in three-dimensional composition space [J].

Ma, H ;

Shi, LL ;

Xu, J ;

Li, Y ;

Ma, E .

APPLIED PHYSICS LETTERS, 2005, 87 (18) :1-3

[12]

Senkov O.N., 2008, METALL MATER TRANS A, V39, P1891

[13]

Speight J.G., 2005, LANGES HDB CHEM, V16th

[14] DUCTILE AL-CU-V AMORPHOUS-ALLOYS WITHOUT METALLOID [J].

TSAI, AP ;

INOUE, A ;

MASUMOTO, T .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (02) :391-393

[15] Roles of minor additions in formation and properties of bulk metallic glasses [J].

Wang, Wei Hua .

PROGRESS IN MATERIALS SCIENCE, 2007, 52 (04) :540-596

[16] Al-rich bulk metallic glasses with plasticity and ultrahigh specific strength [J].

Yang, B. J. ;

Yao, J. H. ;

Zhang, J. ;

Yang, H. W. ;

Wang, J. Q. ;

Ma, E. .

SCRIPTA MATERIALIA, 2009, 61 (04) :423-426

[17] Influence of TM and RE elements on glass formation of the ternary Al-TM-RE systems [J].

Yang, H. ;

Wang, J. Q. ;

Li, Y. .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 2008, 354 (29) :3473-3479

[18] Ductile Bulk Aluminum-Based Alloy with Good Glass-Forming Ability and High Strength [J].

Zhuo Long-Chao ;

Pang Shu-Jie ;

Wang Hui ;

Zhang Tao .

CHINESE PHYSICS LETTERS, 2009, 26 (06)

← 1 2 →