Effects of mechanical properties and layer structure on the cyclic dynamic loading of TiN-based coatings

被引：43

作者：

Chen, Jian ^{[1
]}

Ji, Ran ^{[1
]}

Khan, Raja H. U. ^{[1
]}

Li, Xiaoying ^{[1
]}

Beake, Ben D. ^{[2
]}

Dong, Hanshan ^{[1
,2
]}

机构：

[1] Univ Birmingham, Sch Met & Mat, Birmingham B15 2TT, W Midlands, England

[2] Micro Mat Ltd, Wrexham LL13 7YL, Wales

来源：

SURFACE & COATINGS TECHNOLOGY | 2011年 / 206卷 / 2-3期

关键词：

TiAlSiN; Nano-impact; Focused ion beam; Nanoindentation; WEAR-RESISTANT COATINGS; HARD THIN-FILMS; SI-N COATINGS; IMPACT-WEAR; TRIBOLOGICAL BEHAVIOR; INDENTATION FRACTURE; EROSION RESISTANCE; CUTTING TOOLS; PVD-COATINGS; SINGLE;

D O I：

10.1016/j.surfcoat.2011.07.079

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The cyclic dynamic loading behaviour of a multilayer TiAlSiN coating on M2 steel was systematically investigated using repetitive nano-impact over a wide range of impact load. Its behaviour was compared with a monolayer TIN on the same substrate. When the load was increased to 10 mN and 30 mN for the TiN and TiAlSiN coatings, respectively, cracks started to appear during the tests demonstrated as depth steps in the impact depth curves. The improved crack resistance of TiAlSiN coating is consistent with its higher H/E-r and H-3/E-r(2) measured by nanoindentation. The impact footprints were studied from both top-view and cross-sectional view using a focused ion beam microscope and SEM. Spallation was observed in both coatings at higher impact loads. TiAlSiN coating shows much less spallation due to its multilayer structure. The cross-sectional study discovered that the cracks were initiated within the coating. A simple model has been used to study the power law relationship between the impact volume loss and the impact velocity. (C) 2011 Elsevier B.V. All rights reserved.

引用

页码：522 / 529

页数：8

共 45 条

[1] Impact testing of duplex and non-duplex (Ti,Al)N and Cr-NPVD coatings
Batista, JCA
Godoy, C
Matthews, A
[J]. SURFACE & COATINGS TECHNOLOGY, 2003, 163 : 353 - 361
[2] An investigation of the nanoindentation and nano/micro-tribological behaviour of monolayer, bilayer and trilayer coatings on cemented carbide
Beake, B. D.
Ranganathan, N.
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 423 (1-2): : 46 - 51
[3] Nano-impact testing of TiFeN and TiFeMoN films for dynamic toughness evaluation
Beake, B. D.
Vishnyakov, V. M.
Colligon, J. S.
[J]. JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2011, 44 (08)
[4] Nano-impact testing-an effective tool for assessing the resistance of advanced wear-resistant coatings to fatigue failure and delamination
Beake, BD
Smith, JF
[J]. SURFACE & COATINGS TECHNOLOGY, 2004, 188 : 594 - 598
[5] Evaluating the fracture properties and fatigue wear of tetrahedral amorphous carbon films on silicon by nano-impact testing
Beake, BD
Lau, SR
Smith, JF
[J]. SURFACE & COATINGS TECHNOLOGY, 2004, 177 : 611 - 615
[6] Effect of microstructure on the erosion resistance of Cr-Si-N coatings
Bousser, E.
Benkahoul, M.
Martinu, L.
Klemberg-Sapieha, J. E.
[J]. SURFACE & COATINGS TECHNOLOGY, 2008, 203 (5-7) : 776 - 780
[7] Fracture initiation mechanisms of thin hard coatings during the impact test
Bouzakis, KD
Siganos, A
[J]. SURFACE & COATINGS TECHNOLOGY, 2004, 185 (2-3) : 150 - 159
[8] Creep behaviour determination of monolayer plasma-sprayed coatings under dynamic or static loads
Bouzakis, KD
Lontos, A
[J]. SURFACE & COATINGS TECHNOLOGY, 2003, 174 : 1053 - 1058
[9] Tool wear in cutting plastic - abrasion or erosion?
Budinski, KG
[J]. WEAR, 1999, 233 : 362 - 371
[10] Modelling the hardness response of bulk materials, single and multilayer coatings
Bull, SJ
[J]. THIN SOLID FILMS, 2001, 398 : 291 - 298

← 1 2 3 4 5 →