Literature review of thermal and radiation performance parameters for high-temperature, uranium dioxide fueled cermet materials

被引:52
作者
Haertling, C. [1 ]
Hanrahan, R. J., Jr. [1 ]
机构
[1] Los Alamos Natl Lab, Los Alamos, NM 87545 USA
关键词
D O I
10.1016/j.jnucmat.2007.03.024
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High-temperature fissile-fueled cermet literature was reviewed. Data are presented primarily for the W-UO2 as this was the system most frequently studied; other reviewed systems include cermets with Mo, Re, or alloys as a matrix. Failure mechanisms for the cermets are typically degradation of mechanical integrity and loss of fuel. Mechanical failure can occur through stresses produced from dissimilar expansion coefficients, voids created from diffusion of dissimilar materials or formation of metal hydride and subsequent volume expansion. Fuel loss failure can occur by high temperature surface vaporization or by vaporization after loss of mechanical integrity. Techniques found to aid in retaining fuel include the use of coatings around UO2 fuel particles, use of oxide stabilizers in the UO2, minimizing grain sizes in the metal matrix, minimizing impurities, controlling the cermet sintering atmosphere, and cladding around the cermet. Published by Elsevier B.V.
引用
收藏
页码:317 / 335
页数:19
相关论文
共 27 条
[1]  
Argonne National Laboratory, 1968, ANL7236
[2]  
Baker R.J., 1966, BNWL394
[3]  
BAKER RJ, 1966, NASACR54840
[4]  
BALL LL, 1969, NASATMX1872
[5]  
BATTLES JE, 1967, ANL7235
[6]  
BLANKENSHIP CP, 1968, NAATND4475
[7]  
BURT WR, 1965, ANL7031
[8]  
CARLSON MCJ, 1972, HEDLTME72102
[9]  
Collins J.F., 1969, GEMP741
[10]  
COLLINS J.F, 1968, GEMP659