Effect of Annealing on the Microstructure and Properties of In-situ Cu-Nb Microcomposite Wires

被引：10

作者：

Deng, Li-Ping ^{[1
]}

Wang, Bing-Shu ^{[1
]}

Xiang, Hong-Liang ^{[1
]}

Yang, Xiao-Fang ^{[2
]}

Niu, Rong-Mei ^{[3
]}

Han, Ke ^{[3
]}

机构：

[1] Fuzhou Univ, Sch Mech Engn & Automat, Fuzhou 350116, Peoples R China

[2] Chongqing Univ, Coll Mat Sci & Engn, Chongqing 400044, Peoples R China

[3] Natl High Magnet Field Lab, Tallahassee, FL 32310 USA

来源：

ACTA METALLURGICA SINICA-ENGLISH LETTERS | 2016年 / 29卷 / 07期

基金：

美国国家科学基金会; 中国国家自然科学基金;

关键词：

Annealing; Microstructure; Magnetoresistance; Hardness; Cu-Nb microcomposite wire; MAGNETIC-PROPERTIES; THERMAL-STABILITY; COMPOSITE WIRES; TRANSVERSE MAGNETORESISTANCE; POLYCRYSTALLINE ALUMINUM; INDUCED DIFFUSION; FIELD; RESISTIVITY; COPPER; RECRYSTALLIZATION;

D O I：

10.1007/s40195-016-0432-z

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The effects of annealing on microstructure, magnetoresistance, and hardness of an in situ Cu-Nb microcomposite wire have been investigated. Neither changes in microstructure nor hardness were found until 500 degrees C. Particularly, microstructural change within the Nb films was observed in the annealed samples. The room-temperature magnetoresistivity was almost negligible, while magnetoresistivity at -196 degrees C increased with magnetic field. At temperature above 500 degrees C, recovery and recrystallization occurred, and both the resistance and hardness decreased.

引用

页码：668 / 673

页数：6

共 48 条

[41] CHARACTERIZATION OF THE STRENGTH AND MICROSTRUCTURE OF HEAVILY COLD-WORKED CU-NB COMPOSITES [J].

SPITZIG, WA ;

PELTON, AR ;

LAABS, FC .

ACTA METALLURGICA, 1987, 35 (10) :2427-2442

[42] The effect of a magnetic field upon the electrical resistance of gold and silver at temperatures between 1 and 20 degrees K. [J].

Stout, JW ;

Barieau, RE .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1939, 61 :238-241

[43] Plasticity of multiscale nanofilamentary Cu/Nb composite wires during in situ neutron diffraction: Codeformation and size effect [J].

Thilly, L ;

Renault, PO ;

Vidal, V ;

Lecouturier, F ;

Van Petegem, S ;

Stuhr, U ;

Van Swygenhoven, H .

APPLIED PHYSICS LETTERS, 2006, 88 (19)

[44] Hardness-strength relationships in the aluminum alloy 7010 [J].

Tiryakioglu, M. ;

Robinson, J. S. ;

Salazar-Guapuriche, M. A. ;

Zhao, Y. Y. ;

Eason, P. D. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 631 :196-200

[45] THE RESISTIVITY AND MICROSTRUCTURE OF HEAVILY DRAWN CU-NB ALLOYS [J].

VERHOEVEN, JD ;

DOWNING, HL ;

CHUMBLEY, LS ;

GIBSON, ED .

JOURNAL OF APPLIED PHYSICS, 1989, 65 (03) :1293-1301

[46] OSTWALD RIPENING OF 2-PHASE MIXTURES [J].

VOORHEES, PW .

ANNUAL REVIEW OF MATERIALS SCIENCE, 1992, 22 :197-215

[47]

Zhao B., 2003, ACTA METALL SIN-ENGL, V16, P266

[48] Microstructure and properties of nanostructured Cu28 wt%Ag microcomposite deformed after solidifying under a high magnetic field [J].

Zuo, Xiaowei ;

Han, Ke ;

Zhao, Congcong ;

Niu, Rongmei ;

Wang, Engang .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 619 :319-327

← 1 2 3 4 5 →