Prolonged protection, by zirconium conversion coatings, of AlSi7Mg0.3 aluminium alloy in chloride solution

被引：37
作者：
Sekularac, Gavrilo [1 ,2 ]
Kovac, Janez [3 ]
Milosev, Ingrid [1 ]
机构：
[1] Jozef Stefan Inst, Dept Phys & Organ Chem, Jamova C 39, SI-1000 Ljubljana, Slovenia
[2] Jozef Stefan Int Postgrad Sch, Jamova C 39, SI-1000 Ljubljana, Slovenia
[3] Jozef Stefan Inst, Dept Surface Engn & Optoelect, Jamova C 39, SI-1000 Ljubljana, Slovenia
来源：
CORROSION SCIENCE | 2020年 / 169卷 / 169期
关键词：
Zirconium conversion coating; AlSi7Mg0.3; Active corrosion protection; Self-sealing; CORROSION PROTECTION; INTERMETALLIC PHASES; MECHANICAL-BEHAVIOR; SURFACE; MORPHOLOGY; FLUORIDE; ZINC; RESISTANCE; TITANIUM; LAYERS;
D O I：
10.1016/j.corsci.2020.108615
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Zirconium conversion coatings (ZrCC) were prepared on aluminium alloy AlSi7Mg0.3 by immersion of the latter in 100-500 ppm baths of H2ZrF6. Their electrochemical characterization was carried out while immersed in 0.5 M NaCl for up to 10 days. Immersion tests were performed for up to 28 days. Detailed microstructure characterization of the coatings was carried out prior to and following immersion. The ZrCC-200 coating had a bi-layer structure that was thicker round the intermetallic particles (130-150 nm) than at the matrix (50-60 nm). The corrosion resistance of the ZrCC-200 coating improved during immersion, which was ascribed to transformation of ZrF4/ZrOxFy to ZrO2 center dot xH(2)O((s)) and to formation of Al(OH)(3) in the outermost part of the coating.
引用
收藏
页数：18
相关论文
共 72 条
  • [1] Fluoride-Induced Interfacial Adhesion Loss of Nanoporous Anodic Aluminum Oxide Templates in Aerospace Structures
    Abrahami, S. T.
    de Kok, J. M. M.
    Gudla, V. C.
    Marcoen, K.
    Hauffman, T.
    Ambat, R.
    Mol, J. M. C.
    Terryn, H.
    [J]. ACS APPLIED NANO MATERIALS, 2018, 1 (11): : 6139 - 6149
  • [2] Effect of practical parameters on the structure and corrosion behavior of vanadium/zirconium conversion coating on AA 2024 aluminum alloy
    Ahmadi, P.
    Sarabi, A. A.
    Mohammadloo, H. Eivaz
    Behgam, R.
    [J]. JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2019, 16 (05) : 1503 - 1513
  • [3] SKPFM and SEM study of the deposition mechanism of Zr/Ti based pre-treatment on AA6016 aluminum alloy
    Andreatta, F.
    Turco, A.
    de Graeve, I.
    Terryn, H.
    de Wit, J. H. W.
    Fedrizzi, L.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2007, 201 (18) : 7668 - 7685
  • [4] Addition of phosphates or copper nitrate in a fluotitanate conversion coating containing a silane coupling agent for aluminium alloy AA6014
    Andreatta, F.
    Lanzutti, A.
    Paussa, L.
    Fedrizzi, L.
    [J]. PROGRESS IN ORGANIC COATINGS, 2014, 77 (12) : 2107 - 2115
  • [5] ASTM International, 1998, G5997 ASTM INT
  • [6] Electrochemical characteristics of intermetallic phases in aluminum alloys - An experimental survey and discussion
    Birbilis, N
    Buchheit, RG
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2005, 152 (04) : B140 - B151
  • [7] Birbilis N, 2006, ECS Trans, V1, P115, DOI [10.1149/1.2215495, DOI 10.1149/1.2215495]
  • [8] Bolibruchova D., 2013, 42100 EN AC MAN TECH, P276
  • [9] Bouckenooge P., 2019, USE AES DATA ANAL DE
  • [10] THE DEVELOPMENT OF CHEMICAL CONVERSION COATINGS ON ALUMINUM
    BROWN, GM
    SHIMIZU, K
    KOBAYASHI, K
    THOMPSON, GE
    WOOD, GC
    [J]. CORROSION SCIENCE, 1993, 35 (1-4) : 253 - 256
12345678